The invention relates to a preparation method of super hydrophilic/underwater super-thinning oil polyvinylidene fluoride composite membrane, belonging to the field of environmental functional materials preparation technology; the specific steps are as follows: first, PVDF membrane and PVDF@PDA membrane are prepared; nickel nitrate hexahydrate, cobalt nitrate hexahydrate and urea are dissolved in deionized water to obtain a mixture solution and mix it. The liquid is poured into ethanol, added with PVDF@PDA film, soaked, and then reacted in a reactor, washed and dried with deionized water and ethanol to prepare a PVDF@PDA@NiCo2(OH)6 composite membrane. The membrane separation technology is adopted in the present invention, which has the advantages of short process, easy operation, resource saving and no secondary pollution, and conforms to the concept of green chemistry. It is suitable for wide application.
【技术实现步骤摘要】
一种超亲水/水下超疏油聚偏氟乙烯复合膜的制备方法及其应用
本专利技术涉及一种超亲水/水下超疏油聚偏氟乙烯复合膜的制备方法，属环境功能材料制备
技术介绍
近年来原油开采，海上漏油事故，生活污水等造成的大量的含油废水已成为困扰环境的一大挑战。含油废水会对环境造成了巨大的危害，如石油漂浮在海面上，迅速扩散形成一层不透气的油膜会阻碍水体的复氧作用，导致海洋水体缺氧，影响海洋浮游生物生长，破坏海洋生态平衡。含油污水处理起来也极为困难、效率低、成本高，污水中油按物理状态分为四种：游离油、分散油、乳化油、溶解油。常用于含油废水处理的方法主要有重力法、离心法、气浮法、吸附法，化学法、生物法及膜分离法；目前常用的为膜分离法，因为膜分离具有能耗低、单级分离效率高、过程灵活简单、环境污染低、通用性强等优点；但是膜分离应用效率受膜的抗污染性、热稳定性、化学稳定性等内在因素及膜组件形式、操作条件等外在因素的限制。随着材料科学的发展近年来基于特殊润湿性的表面材料研究发展迅猛，主要包括超亲水、超疏水、超亲油、超疏油、超双疏、超双亲表面等，在自清洁表面，防雾涂层，防污涂层、防指纹涂层，...
【技术保护点】
1.一种超亲水/水下超疏油聚偏氟乙烯复合膜的制备方法，其特征在于，步骤如下：将六水合硝酸镍、六水合硝酸钴、尿素溶解于去离子水中，得到混合液，将混合液倒入乙醇中，加入PVDF@PDA膜，浸泡，然后置于反应釜中进行反应，用去离子水和乙醇冲洗干净，晾干，获得PVDF@PDA@NiCo2(OH)6复合膜。
【技术特征摘要】
1.一种超亲水/水下超疏油聚偏氟乙烯复合膜的制备方法，其特征在于，步骤如下：将六水合硝酸镍、六水合硝酸钴、尿素溶解于去离子水中，得到混合液，将混合液倒入乙醇中，加入PVDF@PDA膜，浸泡，然后置于反应釜中进行反应，用去离子水和乙醇冲洗干净，晾干，获得PVDF@PDA@NiCo2(OH)6复合膜。2.根据权利要求1所述的一种超亲水/水下超疏油聚偏氟乙烯复合膜的制备方法，其特征在于，所述六水合硝酸镍、六水合硝酸钴和尿素的质量比为0.3~0.6:0.6~1.2:0.54~1.08。3.根据权利要求1所述的一种超亲水/水下超疏油聚偏氟乙烯复合膜的制备方法，其特征在于，所述去离...
【专利技术属性】
技术研发人员：王倩倩，崔久云，谢阿田，刘思玮，闫永胜，
申请(专利权)人：江苏大学，
类型：发明
国别省市：江苏,32