The invention relates to a preparation method of polymer membrane for organic small molecule separation based on hydrogel embedded structure. First, a mixture of ethanol /N, methyl pyrrolidone was prepared, and then the polyacrylonitrile polymer was dissolved in it to form a casting liquid and produce a certain degree of microgel. Then the casting film was scraped onto a flat glass plate to control a certain thickness, and then it was placed in deionized water to form a film and was dissolved in alkaline solution. The polymer membrane with hydrogel embedded structure is obtained through modification in the liquid. The invention has the advantages of simplicity, high throughput and portability, provides a new membrane preparation strategy for the separation of organic dyes in water body, and enriches the related research on the combination of macromolecule materials and hydrogel materials.
【技术实现步骤摘要】
基于水凝胶内嵌结构的用于有机小分子分离的高分子膜的制备方法
本专利技术涉及一种用于有机小分子分离的高分子膜的制备方法,具体来说是一种基于水凝胶内嵌结构的用于有机小分子分离的高分子膜的制备方法。
技术介绍
随着印染工业在全世界范围内的快速发展,纺织废水被大量排放。一方面,印染过程消耗大量的水资源,每吨织物的水消耗量多达300m3,这加剧了水危机。另一方面,纺织污水如果没有被正确处理,由于其毒性,它会对环境造成严重威胁并且对人类健康造成严重威胁。纺织废水的有效纯化是极其必要以及重要的。然而,由于纺织废水中含有高浓度的有机物以及复杂成分,纺织废水的有效处理总是十分困难的。包括浮选、吸附、生物降解以及氧化过程的处理方法用于纺织废水的处理,利用仅仅将“污染物”去除或者将大分子化学降解为小分子的方法。但从可持续发展的角度来看,考虑到从纺织废水中提取和再回收珍贵成分的重要性,这些方法是不充分的。压力驱动膜技术是一种可持续发展的科技,在将有机小分子从水中分离出来等领域展现出了极大的潜力。其中,传统的纳滤膜截留分子量(MWCO)为200-1000Da,能够截留水溶性的染料和多价离子 ...
【技术保护点】
1.一种基于水凝胶内嵌结构的用于有机小分子分离的高分子膜的制备方法,其特征在于该方法的具体步骤为:a. 将乙醇和N‑甲基吡咯烷酮按1:40~1:4的体积比混合,在70°C下搅拌10~80 h,充分互溶,得到混合溶剂;b.将聚丙烯腈高分子溶于步骤a所得混合溶剂中,得到质量百分比浓度为5%~18%溶液,60~80 °C下充分机械搅拌,静置48 h脱泡,得到高分子铸膜液;c. 将步骤b得到的高分子铸膜液涂覆到玻璃板上,控制膜的厚度200~300 μm,将该玻璃板置于去离子水中进行相转化10~20 min;d. 将步骤c所得的玻璃板浸没在质量百分比浓度为5%~12%的氢氧化钠溶液中 ...
【技术特征摘要】
1.一种基于水凝胶内嵌结构的用于有机小分子分离的高分子膜的制备方法,其特征在于该方法的具体步骤为:a.将乙醇和N-甲基吡咯烷酮按1:40~1:4的体积比混合,在70°C下搅拌10~80h,充分互溶,得到混合溶剂;b.将聚丙烯腈高分子溶于步骤a所得混合溶剂中,得到质量百分比浓度为5%~18%溶液,60~80°C下充分机械...