The invention discloses a stainless steel alumina-based ceramic composite material, which comprises stainless steel powder, alumina-based ceramic powder and binder. Among them, alumina-based ceramic powder comprises the following components of mass percentage: silica 2-6%, silicon carbide 0.5-2.5%, zirconia 1.5-3.5%, magnesium oxide 0.2-0.9%. The stainless steel powder consists of 12.8-16.5% chromium, 6.2-9.5% nickel, 1.5-3.8% copper, 1-3% manganese, 0.05-0.2% scandium and iron, and the mass percentage of the binder is 3-5%. The invention also discloses a preparation method of stainless steel alumina matrix ceramic composite material, including batching, pressing and roasting processes. The stainless steel alumina ceramic composite material has the advantages of high strength and good density.
【技术实现步骤摘要】
一种不锈钢-氧化铝基陶瓷复合材料及其制备方法
本专利技术涉及不锈钢材料
，特别是涉及一种不锈钢-氧化铝基陶瓷复合材料及其制备方法。
技术介绍
陶瓷增强复合材料由于其增强相成本低、微观结构均匀、材料性能各向同性、可以采用传统的金属加工工艺进行加工，因此引起了人们的广泛关注。316L不锈钢由于具有无磁性、良好的焊接性能及抗蚀性能，在机械、化工、石油、轻工，特别是海洋工程等领域得到广泛使用。然而316L不锈钢属于奥氏体不锈钢，由于本身是固溶体，而且含碳量较低，碳等元素都被固溶在晶格里，冷却时不发生相变，不能通过常用的热处理方式提高其强度和硬度，因此，普通的316L不锈钢强度和硬度都较低，在某些高强度工作条件下往往容易发生破坏，使其在承受较重负荷及对强度有较高要求的设备和部件上的使用受到限制。为此，有必要针对上述问题，提出一种不锈钢-氧化铝基陶瓷复合材料及其制备方法，其能够解决现有技术中存在的问题。
技术实现思路
本专利技术的目的在于提供一种不锈钢-氧化铝基陶瓷复合材料及其制备方法，以克服现有技术中的不足。为实现上述目的，本专利技术提供如下技术方案：一种不锈钢-氧化铝基...
【技术保护点】
1.一种不锈钢‑氧化铝基陶瓷复合材料，其特征在于，包括不锈钢粉末、氧化铝基陶瓷粉末及粘结剂，其中，氧化铝基陶瓷粉末包括下述质量百分比的成分：二氧化硅2～6％，碳化硅0.5～2.5％，二氧化锆1.5～3.5％，氧化镁0.2～0.9％，余量为氧化铝；所述不锈钢粉末包括下述质量百分比的成分：铬为12.8～16.5％，镍为6.2～9.5％，铜为1.5～3.8％，锰为1～3％，钪0.05～0.2％，余量为铁；所述粘结剂的质量百分比为3～5％。
【技术特征摘要】
1.一种不锈钢-氧化铝基陶瓷复合材料，其特征在于，包括不锈钢粉末、氧化铝基陶瓷粉末及粘结剂，其中，氧化铝基陶瓷粉末包括下述质量百分比的成分：二氧化硅2～6％，碳化硅0.5～2.5％，二氧化锆1.5～3.5％，氧化镁0.2～0.9％，余量为氧化铝；所述不锈钢粉末包括下述质量百分比的成分：铬为12.8～16.5％，镍为6.2～9.5％，铜为1.5～3.8％，锰为1～3％，钪0.05～0.2％，余量为铁；所述粘结剂的质量百分比为3～5％。2.根据权利要求1所述的不锈钢-氧化铝基陶瓷复合材料，其特征在于，所述不锈钢基体的质量百分比为72～80％，所述氧化铝基陶瓷粉末的质量百分比为15～25％。3.根据权利要求2所述的不锈钢-氧化铝基陶瓷复合材料，其特征在于，所述不锈钢基体的质量百分比为75～78％，所述氧化铝基陶瓷粉末的质量百分比为17～22％。4.根据权利要求1所述的不锈钢-氧化...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。