The invention relates to the field of nano-material preparation technology, in particular to a preparation method of oil-soluble fluorescent TMDs quantum dots and their colloids, including: (1) adding transition metal sulfide compounds to cyclohexanone to prepare suspension; (2) heating and reflux treatment of suspension, cooling and stationary after reflux; (3) taking supernatant clearance after stationary. Oil-soluble TMDs quantum dots were obtained by centrifugal treatment of the liquid and rotational distillation of the supernatant after centrifugation. The invention has the advantages of simple method, mild and safe conditions, low equipment cost, high preparation efficiency and no need for later purification treatment.
【技术实现步骤摘要】
油溶性荧光TMDs量子点及其胶体的制备方法
本专利技术涉及纳米材料制备
，特别涉及一种油溶性荧光TMDs量子点及其胶体的制备方法。
技术介绍
量子点(QuantumDots，QDs)是零维纳米半导体材料，具有一系列独特光电性质，在太阳能电池、发光器件、生物医学等领域有广泛应用。二维过渡金属硫族化合物(TMDs)是指由过渡族金属元素(M)和硫族非金属元素(X)所形成的X-M-X类三明治结构化合物，例如MoS2、WS2等。一直以来人们对TMDs研究主要集中在微米和纳米尺度。随着材料技术发展，人们发现通过进一步减小材料尺寸，MoS2、WS2可从间接带隙突变直接带隙材料，其物理、化学性质发生突变，如具有较高荧光量子产率、消光系数、抗漂泊能力、较宽激发光谱范围以及超高电子转移速率等。可应用于荧光油墨、光电器件、生物标记、荧光探针等领域。目前荧光电子材料油墨的基体材料，以II－VI族量子点为主，如CdSe、CdSe/CdS等，其中镉等有害重金属，不利于环境保护。另外，发射波长为400-500nmII－VI族量子点的制备还相当困难。而MoS2、WS2量子点发射光谱区间恰好...
【技术保护点】
1.一种油溶性荧光TMDs量子点的制备方法，其特征在于，包括如下步骤：(1)向环己酮中加入过渡金属硫化合物，制成悬浊液；(2)对悬浊液进行加热回流处理，回流结束后冷却静置；(3)取静置后的上层清液进行离心处理，之后收集离心后的上清液进行旋转蒸馏，得到油溶性TMDs量子点。
【技术特征摘要】
1.一种油溶性荧光TMDs量子点的制备方法，其特征在于，包括如下步骤：(1)向环己酮中加入过渡金属硫化合物，制成悬浊液；(2)对悬浊液进行加热回流处理，回流结束后冷却静置；(3)取静置后的上层清液进行离心处理，之后收集离心后的上清液进行旋转蒸馏，得到油溶性TMDs量子点。2.根据权利要求1所述油溶性荧光TMDs量子点制备方法，其特征在于：所述步骤(1)中过渡金属硫化合物为MoS2或WS2。3.根据权利要求1所述油溶性荧光TMDs量子点的制备方法，其特征在于：所述步骤(1)中过渡金属硫化合物与环己酮按照10-400mg：10-100ml的质量体积比混合。4.根据权利要求3所述油溶性荧光TMDs量子点的制备方法，其特征在于：所述步骤(1)采用磁力搅拌方式进行混合，混合时间为8-12分钟。5.根据权利要求1所述油溶性荧光TMDs量子点的制备方法，...
【专利技术属性】
技术研发人员：吴凤义，蒋阳，陈敏，胥恩泽，汪海燕，杨绳岩，高立，王志海，吴凤彬，
申请(专利权)人：巢湖学院，
类型：发明
国别省市：安徽,34