The invention discloses a red phosphor and a preparation method thereof, in which the raw material of NaF powder is first calcined at 500 C for half an hour in a tubular furnace, and then quickly taken out of a tubular furnace at 500 C for natural cooling, and the raw material of NaF powder is obtained by dry ball milling for 6 hours; and then the raw material is weighed according to the stoichiometric ratio of Na2TiWO5F2: xEu3 +. The corresponding raw materials, 0.01 < x < 0.1, and then through ball milling, high temperature pre-firing, and then ball milling to get red phosphor materials, the preparation method is simple, suitable for large-scale production. Na2TiWO5F2:xEu3+ synthesized by this method has good fluorescence thermal stability, and the excitation wavelength matches the output wavelength of near ultraviolet LED chip or blue LED chip. It is a new and efficient red phosphor material for white LED.
【技术实现步骤摘要】
一种红色荧光粉及其制备方法本申请是申请号为2016109678866，申请日为2016年11月05日，专利技术创造名称为“含氟钨酸盐红色荧光粉及其制备方法”的专利的分案申请。
本专利技术涉及一种荧光粉及其制备方法，尤其适用于白光LED用的含氟钨酸盐红色荧光粉及其制备方法，属于无机发光材料
技术介绍
近年来，节能照明产业高速发展，白光LED作为新型环保照明产品，具有节能、高效、寿命长、体积小等优点，已经得到了广泛应用。目前实现白光LED主要有以下3种途径：①用大功率GaN蓝色LED芯片激发以YAG为基质的荧光粉，通过蓝色芯片发出的光和被其激发出的黄光混合而得到白光，但这种方法获得的白光显色指数普遍不高，因为缺少红色组分；②集成R、G、B三基色LED芯片并封装在单个器件内，通过调节三基色的配比和相应芯片的电流便可实现白光，这种方法涉及3种电流电压不同的3种芯片，长期点亮下色温会容易漂移；③通过紫外可见LED结合RGB荧光粉而得到白光，通过这种方式获得的白光不仅显色指数高而且成本低。目前灯用三基色荧光粉是用在照明领域最多的，而且红色荧光粉能够提高白光LED的色...
【技术保护点】
1.一种红色荧光粉，其特征在于所述荧光粉具有如下化学表示式：Na2TiWO5F2:xEu3+，其中，0.01≤x≤0.1。
【技术特征摘要】
1.一种红色荧光粉，其特征在于所述荧光粉具有如下化学表示式：Na2TiWO5F2:xEu3+，其中，0.01≤x≤0.1。2.一种红色荧光粉的制备方法，其特征在于：所述荧光粉的制备方法具体步骤为：(1)将NaF粉末原料在管式炉中500℃煅烧半小时，然后直接从500℃的管式炉中快速取出并置于室温中自然冷却后，将粉末原料干式球磨6小时，待用；(2)按化学表示式Na2TiWO5F2:xEu3+的化学计量比称取相应的粉末原料，所述粉末原料分别为NaF、TiO2、WO3和Eu2O3，其中0...
【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：惠安县云点网络科技有限公司，
类型：发明
国别省市：福建,35