The invention relates to a nanometer calcium hydroxide/magnesium aluminum carbonate nanometer hydrotalcite nanometer composite material and a preparation method thereof. First, magnesium aluminum carbonate nanometer hydrotalcite is synthesized by hydrothermal synthesis method. Then the Mg-Al-C Nano-Hydrotalcite was added into the precursor solution of calcium hydroxide, and the nano-composite was synthesized by solution method. The process is simple and yields large. The application results show that it only takes about 6 hours for nano-calcium hydroxide/nano-hydrotalcite nano-composites to be applied and strengthened, which greatly improves the work efficiency of cultural relics protection. At the same time, the mural strengthened by nano calcium hydroxide / nano hydrotalcite nanocomposites was reinforced by NO3.
【技术实现步骤摘要】
纳米氢氧化钙/镁铝碳酸根型纳米水滑石纳米复合材料及制备方法
本专利技术属于材料制备领域，涉及一种纳米氢氧化钙/镁铝碳酸根型纳米水滑石纳米复合材料及制备方法。
技术介绍
纳米水滑石材料属于阴离子型层状化合物。层状化合物是指具有层状结构、层间离子，具有可交换性的一类化合物，利用层状化合物主体在强极性分子作用下所具有的可插层性和层间离子的可交换性，将一些功能性客体物质引入层间空隙并将层板距离撑开从而形成层柱化合物。(BingLi等，JournalofAlloysandCompounds2016,673,265)。典型的水滑石是镁铝碳酸根型水滑石：Mg6Al2(OH)16CO3·4H2O。其结构为由MgO6八面体共用棱形成单元层，位于层上的Mg2+可在一定的范围内被Al3+同晶取代，使得层板带正电荷，层间有可交换的CO32-与层板上的正电荷平衡，使得其整体结构呈电中性。由于层板和层间阴离子通过氢键连接，使得它层间阴离子具有可交换性。CO32-,NO3-,Cl-,OH-,SO42-,PO43-等离子可以在其层间交换。因此它常常被用作离子交换剂。(MengqiangZhao等...
【技术保护点】
1.一种纳米氢氧化钙/纳镁铝碳酸根型米水滑石纳米复合材料，其特征在于包括纳米氢氧化钙和镁铝碳酸根型纳米水滑石，其中镁铝碳酸根型纳米水滑石的质量百分比为30％‑45％，余量为纳米氢氧化钙。
【技术特征摘要】
1.一种纳米氢氧化钙/纳镁铝碳酸根型米水滑石纳米复合材料，其特征在于包括纳米氢氧化钙和镁铝碳酸根型纳米水滑石，其中镁铝碳酸根型纳米水滑石的质量百分比为30％-45％，余量为纳米氢氧化钙。2.一种制备权利要求1所述纳米氢氧化钙/镁铝碳酸根型纳米水滑石纳米复合材料的方法，其特征在于步骤如下：步骤1、镁铝碳酸根型纳米水滑石的制备：将MgCl2·6H2O和AlCl3·6H2O溶于去离子水中制成溶液，将溶液滴加于氢氧化钠溶液中沉淀；将得到沉淀物离心并分散于100-150ml的0.1-0.2摩尔/升的碳酸钠溶液中静置6-10h；将静置后的溶液离心洗涤，并转移到反应釜中在100-120度条件下反应5-10小时；反应完毕后将过滤干燥即得到镁铝碳酸根型纳米水滑石的粉体；所述MgCl2·...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。