The invention relates to an anti-corrosion method for metal components, in which the edges and corners of metal components are chamfered by arc processing, the edges and corners of the metal components are machined into arc chamfered parts, and then the arc chamfered parts are heat treated, and the surface of the metal components is painted with anti-corrosion paint after heat treatment. By treating the edges and corners of metal components with arc chamfering and further optimizing through heat treatment, the following paint film can be uniformly distributed, the paint film is not easy to be corroded, the service life of the paint film is significantly prolonged, and the anticorrosion protection life of the paint film for metal components is greatly improved.
【技术实现步骤摘要】
一种金属构件防腐方法
本专利技术涉及一种金属构件防腐方法，属于建筑安装
技术介绍
目前，在电解、净液、尾气处理等钢结构建筑安装项目中，钢结构建筑易被腐蚀性，虽然除锈、防腐的施工要求高于一般场所，但是置于这种环境的铁构件在使用一两年后均出现不同程度的腐蚀。其腐蚀通常都是先从带有棱角的边缘处开始，再从边缘处沿着金属表面防腐层内开始逐步向周边扩展开，最后致使全构件腐蚀。
技术实现思路
本专利技术针对现有技术存在的不足，提供了一种金属构件防腐方法，具体技术方案如下：一种金属构件防腐方法，对金属构件的棱角进行圆弧倒角处理，然后对金属构件的表面进行涂刷防腐漆。作为上述技术方案的改进，使用砂轮机对金属构件的棱角进行圆弧倒角处理。作为上述技术方案的改进，对金属构件的棱角进行圆弧倒角处理后，金属构件的棱角被加工成圆弧倒角部，圆弧倒角部中圆弧的半径大于4mm。作为上述技术方案的改进，对金属构件的棱角进行圆弧倒角处理，金属构件的棱角被加工成圆弧倒角部，再对圆弧倒角部进行热处理，热处理完毕对金属构件的表面进行涂刷防腐漆。作为上述技术方案的改进，所述热处理过程如下：在圆弧倒角部的表面...
【技术保护点】
1.一种金属构件防腐方法，其特征在于：对金属构件的棱角进行圆弧倒角处理，然后对金属构件的表面进行涂刷防腐漆。
【技术特征摘要】
1.一种金属构件防腐方法，其特征在于：对金属构件的棱角进行圆弧倒角处理，然后对金属构件的表面进行涂刷防腐漆。2.根据权利要求1所述的一种金属构件防腐方法，其特征在于：使用砂轮机对金属构件的棱角进行圆弧倒角处理。3.根据权利要求1所述的一种金属构件防腐方法，其特征在于：对金属构件的棱角进行圆弧倒角处理后，金属构件的棱角被加工成圆弧倒角部，圆弧倒角部中圆弧的半径大于4mm。4.根据权利要...
【专利技术属性】
技术研发人员：何俊峰，
申请(专利权)人：铜陵有色金属集团铜冠建筑安装股份有限公司，
类型：发明
国别省市：安徽,34