The invention discloses an anti-mildew treatment method for bamboo products, which comprises the following steps: S1, cutting bamboo, cleaning and drying, and then microwave treatment to obtain pre-treated bamboo; S2, soaking and cleaning the pre-treated bamboo in a vegetable ash solution, then soaking in a moth-proof solution and draining water after soaking; The bamboo treated in S2 was dried and carbonized, in which the bamboo was put into a drying and disinfecting carbon dryer, and the heating temperature of the drying and disinfecting carbon dryer was 160-190 C, the heating time was 2-4 hours, and the bamboo was carbonized with a degree of 5-30%.
【技术实现步骤摘要】
一种竹制品防霉变处理方法
本专利技术涉及竹制品
,尤其涉及一种竹制品防霉变处理方法。
技术介绍
竹制品是指以竹子为加工原料制造的产品,以其绿色环保而深受消费者欢迎。由于竹子中因含有淀粉、脂肪、蜡质、糖类、蛋白质和矿物质等化合物,能给许多种类的细菌提供充足的营养物质,在使用过程中容易发生霉变现象,影响竹制品的使用寿命。
技术实现思路
基于
技术介绍
存在的技术问题,本专利技术提出了一种竹制品防霉变处理方法,有效防止竹制品出现霉变和虫蛀等现象,在提高竹制品品质的同时并延长了竹制品使用寿命。为实现上述目的,本专利技术通过如下技术方案加以实现:一种竹制品防霉变处理方法,包括以下步骤:S1、将竹材切段,清洗,干燥,然后进行微波处理,得到预处理竹材;S2、将预处理竹材置于草木灰溶液中浸泡,清洗,然后置于防蛀液中浸泡,浸泡后沥干水分;S3、将S2中处理得到的竹材进行干燥碳化处理,其中碳化处理为将竹材放入烘干消毒碳干机,烘干消毒碳干机加热的温度为160—190℃,加热时间2—4小时,竹材碳化,碳化程度为5%—30%。作为优选,S1中,微波处理过程如下:将干燥后的竹材在12-18KW微波功率下加热10-15min,然后在22-28KW微波功率下加热5-8min,再在60-70KW微波功率下加热1-2min。作为优选,S2中,将预处理竹材置于草木灰溶液中浸泡2-3h,清洗,然后置于防蛀液中,在30-35℃温度条件下浸泡1-2h,浸泡后沥干水分。作为优选,S2中,防蛀液的原料按重量份包括:石蜡乳液10-20份、氨基硅油15-25份、纳米凹凸棒土6-12份、壳聚糖铜盐0.4-0.8 ...
【技术保护点】
1.一种竹制品防霉变处理方法,其特征在于,包括以下步骤:S1、将竹材切段,清洗,干燥,然后进行微波处理,得到预处理竹材;S2、将预处理竹材置于草木灰溶液中浸泡,清洗,然后置于防蛀液中浸泡,浸泡后沥干水分;S3、将S2中处理得到的竹材进行干燥碳化处理,其中碳化处理为将竹材放入烘干消毒碳干机,烘干消毒碳干机加热的温度为160—190℃,加热时间2—4小时,竹材碳化,碳化程度为5%—30%。
【技术特征摘要】
1.一种竹制品防霉变处理方法,其特征在于,包括以下步骤:S1、将竹材切段,清洗,干燥,然后进行微波处理,得到预处理竹材;S2、将预处理竹材置于草木灰溶液中浸泡,清洗,然后置于防蛀液中浸泡,浸泡后沥干水分;S3、将S2中处理得到的竹材进行干燥碳化处理,其中碳化处理为将竹材放入烘干消毒碳干机,烘干消毒碳干机加热的温度为160—190℃,加热时间2—4小时,竹材碳化,碳化程度为5%—30%。2.根据权利要求1所述竹制品防霉变处理方法,其特征在于,S1中,微波处理过程如下:将干燥后的竹材在12-18KW微波功率下加热10-15min,然后在22-28KW微波功率...