The invention discloses a crack-resistant high-strength insulation brick. The raw materials include: Portland cement 60 100, rice husk composite 10 20, magnesite cement 30 80, cinder 2 10, sepiolite powder 4 10, microcrystalline cellulose 1 3, talc powder 4 9, early strength agent 1 2, reinforcing agent 1 2, water 50. 150, 1, 3, 3, 1, 2, and 0.2. Rice husk composite was prepared by adding rice husk into potassium hydroxide solution, stirring at elevated temperature, filtering, vacuum drying, adding graphene oxide to mix evenly, carbonizing, grinding evenly, adding glycerol, sodium polyacrylate, water to stir, adding hydroiodic acid to stir, filtering, washing, drying to get rice husk composite. The anti-cracking high-strength thermal insulation brick has the advantages of high toughness, non-cracking, high strength and good thermal insulation effect.
【技术实现步骤摘要】
一种抗开裂高强度保温砖
本专利技术涉及保温砖
，尤其涉及一种抗开裂高强度保温砖。
技术介绍
保温墙体砖用于堆砌墙体，是近几年才开始的，现有的节能建筑墙体采用的节能保温措施是在采用保温砖进行堆砌。我国矿产资源80％为共伴生矿，大量有价值资源存留于尾矿之中，尾矿堆存需要占用大量土地。很多尾矿库超期或超负荷使用，甚至违规操作，使尾矿库存在极大的安全隐患，对周边地区的人民财产和生命安全造成严重威胁。如果将尾矿用来制备保温砖，将极大地节约成本投入，但建筑使用中可能会出现开裂的问题，造成安全隐患。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种抗开裂高强度保温砖，韧性极高，不易开裂，而且强度高，保温效果好。本专利技术提出的一种抗开裂高强度保温砖，其原料按重量份包括：硅酸盐水泥60-100份，稻壳复合物10-20份，菱镁水泥30-80份，煤渣2-10份，海泡石粉4-10份，微晶纤维素1-3份，滑石粉4-9份，早强剂1-2份，增强剂1-2份，水50-150份，聚苯乙烯泡沫颗粒1-3份，胶质剂1-2份，液体发泡剂0.2-1份。优选地，稻壳复合物采用如下工艺制备：将...
【技术保护点】
1.一种抗开裂高强度保温砖，其特征在于，其原料按重量份包括：硅酸盐水泥60‑100份，稻壳复合物10‑20份，菱镁水泥30‑80份，煤渣2‑10份，海泡石粉4‑10份，微晶纤维素1‑3份，滑石粉4‑9份，早强剂1‑2份，增强剂1‑2份，水50‑150份，聚苯乙烯泡沫颗粒1‑3份，胶质剂1‑2份，液体发泡剂0.2‑1份。
【技术特征摘要】
1.一种抗开裂高强度保温砖，其特征在于，其原料按重量份包括：硅酸盐水泥60-100份，稻壳复合物10-20份，菱镁水泥30-80份，煤渣2-10份，海泡石粉4-10份，微晶纤维素1-3份，滑石粉4-9份，早强剂1-2份，增强剂1-2份，水50-150份，聚苯乙烯泡沫颗粒1-3份，胶质剂1-2份，液体发泡剂0.2-1份。2.根据权利要求1所述抗开裂高强度保温砖，其特征在于，稻壳复合物采用如下工艺制备：将稻壳加入氢氧化钾溶液中，升温搅拌，过滤，真空干燥，加入氧化石墨烯混合均匀，碳化，研磨均匀，加入甘油、聚丙烯酸钠、水搅拌，加入氢碘酸搅拌，过滤，洗涤，干燥得到稻壳复合物。3.根据权利要求2所述抗开裂高强度保温砖，其特征在于，稻壳复合物的制备工艺...
【专利技术属性】
技术研发人员：奚程翀，
申请(专利权)人：安徽润晟建设有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。