The invention relates to the manufacturing process of lightning arresters, and more specifically relates to a new sealing manufacturing process of metal oxide lightning arresters with porcelain jackets. Through cleaning, preheating, gluing, exhaust and other operating steps, a new sealing manufacturing process of metal oxide lightning arrester for porcelain jacket can be realized. The ceramic jacket lightning arrester adopts double sealing manufacturing process, the sealing performance has been greatly improved, and the water vapor produced by the change of air pressure and temperature in the porcelain jacket and the side branch of the resistor sheet can be prevented. A discharge trace occurs to prolong the service life of the arrester.
【技术实现步骤摘要】
一种瓷外套金属氧化物避雷器新型密封制造工艺
本专利技术涉及避雷器制造工艺，更具体地，涉及一种瓷外套金属氧化物避雷器新型密封制造工艺。
技术介绍
密封是避雷器的生命线，避雷器因密封不良而造成事故，退出运行的问题经常发生的。根据运行经验，95%的瓷外套避雷器的故障，是密封及其引起的综合作用造成的。传统的瓷外套避雷器的内部结构大致为：非线性电阻片配好组后叠起，上部装一个弹簧，下部配置金属垫块装入瓷套内密封起来。避雷器装配好后，内部空腔随着温度、气压变化，形成1个微循环的小气候。气温高时，空气中可容纳水分就多；而当晚上温度降低时，空气中所能容纳的水分减少，如装配时没采取降温去湿措施，微量水分会在避雷器内部形成凝露，吸附在避雷器元件的各个表面（瓷套、电阻片组），其中瓷套内壁是不吸水并耐电弧灼烧的。电阻片侧面釉是有机涂复层，吸水率高，不耐漏电起痕。因在运行时电阻片流过有一定的持续电流和温升，故水分一般会凝结在电阻片表面，当集聚到一定程度时会形成局部通道放电。水分在电弧作用下扩散，然后重新集聚，周而复始，在电阻片侧面上形成树枝状放电痕迹。在潮湿、局部放电、电晕作用下，使避雷器内...
【技术保护点】
1.一种瓷外套金属氧化物避雷器新型密封制造工艺，其特征在于，包括以下步骤：S1：金属氧化物避雷器的瓷套和避雷器阀片组装配前采用三氯三氟乙烯溶剂清洗；S2：将瓷件、芯棒两头均匀地涂上底涂剂，然后将芯棒放入瓷套中；S3：将配好芯棒的瓷件放到烤温箱里升温到40～50度，烘2‑3小时预热；S4：将预热好的瓷件从烘箱中拿出来，从瓷件中取出芯棒，将胶沿瓷件壁灌入，然后在芯棒四周均匀涂上一层胶，再把芯棒放入瓷件中，让其自然滑下至底部，保证芯棒不偏向一面，多胶的挖出少胶的补上，芯棒与瓷件内壁之间没有缝隙，然后将瓷件表面的硅胶清理干净；S5：将灌好胶的瓷件放入负压检漏仪中，排出空隙内多余的空...
【技术特征摘要】
1.一种瓷外套金属氧化物避雷器新型密封制造工艺，其特征在于，包括以下步骤：S1：金属氧化物避雷器的瓷套和避雷器阀片组装配前采用三氯三氟乙烯溶剂清洗；S2：将瓷件、芯棒两头均匀地涂上底涂剂，然后将芯棒放入瓷套中；S3：将配好芯棒的瓷件放到烤温箱里升温到40～50度，烘2-3小时预热；S4：将预热好的瓷件从烘箱中拿出来，从瓷件中取出芯棒，将胶沿瓷件壁灌入，然后在芯棒四周均匀涂上一层胶，再把芯棒放入瓷件中，让其自然滑下至底部，保证芯棒不偏向一...