一种抗老化的彩色沥青制造技术

本发明专利技术公开了一种抗老化的彩色沥青，其由如下重量份数的原料制成：C5石油树脂15‑20份、C9石油树脂20‑30份、基础油30‑35份、丁苯橡胶粉3‑8份、无机颜料5‑12份、抗老化剂0.8‑1.2份。本发明专利技术可以生产出各种色彩的彩色沥青，改善视觉，可以广泛地应用在街道、人行道及景观道等不同场所，不仅可以满足各种场所的需求，同时还可以美化环境。本发明专利技术通过配方整体设计，实现了以较低成本制备得到性能优异的彩色沥青产品。

An anti aging color asphalt

The invention discloses an anti-aging colored asphalt, which is made from the following raw materials: C5 petroleum resin 15 20, C9 petroleum resin 20 30, base oil 30 35, styrene-butadiene rubber powder 3 8, inorganic pigment 5 12, anti-aging agent 0.8 1.2. The invention can produce colored asphalt of various colors, improve vision, and can be widely used in different places, such as streets, sidewalks and landscape roads. It can not only meet the needs of various places, but also beautify the environment. The invention realizes the preparation of color asphalt products with excellent performance at lower cost by the integral design of the formula.

【技术实现步骤摘要】
一种抗老化的彩色沥青
本专利技术涉及道路工程
，特别是涉及了一种抗老化的彩色沥青。
技术介绍
彩色沥青路面具有普通沥青混凝土的弹性强、减振性强和容易清扫冲洗等良好性能外，还改善了普通沥青路面黑色的单调性，可以与周围的建筑、景观相互搭配、协调，具有明显的景观效益。此外，彩色沥青对交通的组织和管理作用日益得到人们的重视。不同颜色的沥青路面，可以提高驾驶员的识别效果，而且还能使驾驶员的注意力更加集中，从而起到诱导车流、安全行车、使交通管理直观化的作用。例如在城市道路交通事故多发地段，可以铺筑红色或黄色路面，直观地提醒驾驶员注意，谨慎行车，在某种程度上比垂直的交通标志以及在车道上划标志线更好。但是现有的彩色沥青的性能仍然有待提高。
技术实现思路
为了弥补已有技术的缺陷，本专利技术提供一种抗老化的彩色沥青。本专利技术所要解决的技术问题通过以下技术方案予以实现：一种抗老化的彩色沥青，其由如下重量份数的原料制成：C5石油树脂15-20份、C9石油树脂20-30份、基础油30-35份、丁苯橡胶粉3-8份、无机颜料5-12份、抗老化剂0.8-1.2份。进一步地，所述基础油为矿物类油。进一步地，无机颜本文档来自技高网...

【技术保护点】
1.一种抗老化的彩色沥青，其由如下重量份数的原料制成：C5石油树脂15‑20份、C9石油树脂20‑30份、基础油30‑35份、丁苯橡胶粉3‑8份、无机颜料5‑12份、抗老化剂0.8‑1.2份。

【技术特征摘要】
1.一种抗老化的彩色沥青，其由如下重量份数的原料制成：C5石油树脂15-20份、C9石油树脂20-30份、基础油30-35份、丁苯橡胶粉3-8份、无机颜料5-12份、抗老化剂0.8-1.2份。2.如权利要求1所述的抗老化的彩色沥青，其特征在于，所述基础油为矿物类油。3.如权利要求1所述的抗老化的彩色沥青，其特征在于，无机颜料为铁红颜料、铬绿颜料、铁绿颜料、钛白颜料、铬黄颜料中的至少一种。...