The invention discloses a high elastic fluorine rubber and a preparation method thereof, including 45-65 phr of raw fluorine rubber modified, 10-20 phr of silica filler, 10-15 phr of alcohol release agent, 5-10 phr of chloroplatinic acid vulcanizing agent, 5-10 phr of triphenylphosphine accelerator, 5-10 phr of hydroxyl silicone oil, 10-20 phr of fatty acid zinc and 5-10 phr of polypropylene. Mixture A was obtained by mixing fatty acid zinc, polypropylene, silica filler and triphenylphosphine accelerator, then mixing alcohol demoulding agent, chloroplatinic acid vulcanizing agent and hydroxyl silicone oil to form mixture B. Mixture A, mixture B and modified fluororubber raw rubber were stirred evenly at 200-250 C and then removed. Natural cooling. The invention takes chloroplatinic acid as vulcanizing agent, silica as filling agent and adopts a new mold release agent WS280, which can effectively improve the fluidity and adhesion of fluororubber, and improve the vulcanizing property, elasticity and strength of fluororubber.
【技术实现步骤摘要】
一种高弹氟橡胶及其制备方法
本专利技术涉及一种高弹氟橡胶及其制备方法，属于氟橡胶制备领域。
技术介绍
在橡胶工业中，氟橡胶具有其他橡胶无可比拟的优异性能，如耐高温、耐油、耐各种强酸强碱及化学品的腐蚀，抗臭氧及各种氧化剂，抗辐射等特性。氟橡胶已广泛应用于军工航天、石油化工、机械制造、建筑工程、仪器仪表及汽车制造等领域。氟橡胶的特殊性能是由于其分子中含有氟原子的结构特性所决定的，但正是由于这种结构特点，其分散性及粘接性能较差，给氟橡胶在性能上存在一些不足，为此人们对氟橡胶的改进做了各种研究。
技术实现思路
专利技术目的：本专利技术所要解决的技术问题是针对现有技术的不足，提供一种硫化性能好，强度高的高弹氟橡胶及其制备方法。为了解决上述技术问题，本专利技术公开了一种高弹氟橡胶，包括如下重量份的组份：优选地，所述氟橡胶包括如下重量份的组份：其中，所述改性氟橡胶生胶为氟橡胶26或氟橡胶246。所述醇类脱模剂为德国struktolWS280。所述氯铂酸硫化剂产自苏州金沃化工有限公司。所述三苯基膦促进剂产自苏州锦源精细化工有限责任公司。本专利技术还提供上述高弹氟橡胶的制备方法，包括如...
【技术保护点】
1.一种高弹氟橡胶，其特征在于，所述氟橡胶包括如下重量份的组份：
【技术特征摘要】
1.一种高弹氟橡胶，其特征在于，所述氟橡胶包括如下重量份的组份：2.根据权利要求1所述的一种高弹氟橡胶，其特征在于，所述氟橡胶包括如下重量份的组份：3.根据权利要求1或2所述的一种高弹氟橡胶，其特征在于，所述改性氟橡胶生胶为氟橡胶26或氟橡胶246。4.根据权利要求1或2所述的一种高弹氟橡胶，其特征在于，所述醇类脱模剂为德国struktolWS280。5.根据权利要求1或2所述的一种高弹氟橡胶，其特征在于，所述氯铂酸硫化剂产自苏州金沃化工有限公司。6.根据权利要求1或2所述的一种高弹氟橡胶，其特征在...