The invention discloses a method for preparing 3D MnO2/Ni composite material. The steps are as follows: the foamed nickel with size 2.5cm * 1.5cm is placed in acetone and ethanol solution respectively for ultrasonic 25 35min, then is immersed in hydrochloric acid solution to etch 20 30min 30min, then washed with a large amount of deionized water, and then dried in an oven at 52 58 degrees Celsius. The manganese acetate and ammonium acetate are dissolved in distilled water. The nickel foam is placed in the above solution and deposited under 35 0.9mA/cm2 of current density at 0.7 45min. After the electrodeposition is finished, the Ni net is removed, washed and dried at 55 and 65 degrees. The method is simple, rapid and easy to operate. The 3D_MnO2/Ni composite has high discharge specific capacity and good cycling performance.
【技术实现步骤摘要】
一种制备3D-MnO2/Ni复合材料的方法
本专利技术涉及一种制备3D-MnO2/Ni复合材料的方法。
技术介绍
化石燃料广泛使用使得全球经济迅速增长，同时也带来了2个问题：一是加速了化石燃料的耗尽，二是带来了环境问题，如加速了温室气体的排放、导致了水和空气的污染。如何在可持续发展下开发新的清洁能源是世界各地共同关心的主要问题，也是我国社会经济发展的重要课题。为了实现低碳经济和使用清洁的可再生能源，人类社会离不开发展和使用先进能源存储技术。如今世界大部分国家使用的可再生清洁能源是依赖太阳能、风力和其他可再生能源。但是，这些能源的输出受气象条件、地域以及时间等因素所限制，并且发生某些地区能源过剩而有些地区能源不足的情况，因此，有必要开发能量储存及转换的系统。电池、燃料电池和电化学超级电容器被公认为是3种最重要的电化学储存和转换设备。超级电容器学术上也叫电化学电容器。由于该装置具有在数秒内进行完全充放电、循环性能极好、功率密度高等优点已经在学术界和产业界引起广泛的关注。到目前为止，应用于超级电容器的电极材料主要有碳材料、金属氧化物/氢氧化物，以及导电聚合物，每一种电极...
【技术保护点】
1.一种制备3D‑MnO2/Ni复合材料的方法，其特征在于包括如下步骤：将大小为2.5cm×1.5cm的泡沫镍置于丙酮、乙醇溶液中分别超声25‑35min，然后浸于浓度为1mol/L的盐酸溶液中刻蚀20‑30min，用大量的去离子水洗净后，放于52‑58℃的烘箱内干燥，备用；将15‑25份醋酸锰和20‑30份醋酸铵溶于90‑100份蒸馏水中，将泡沫镍置于上述溶液中，在0.7‑0.9mA/cm2的电流密度下沉积35‑45min，待电沉积完后，取出Ni网，水洗，55‑65℃干燥即得；各原料均为重量份。
【技术特征摘要】
1.一种制备3D-MnO2/Ni复合材料的方法，其特征在于包括如下步骤：将大小为2.5cm×1.5cm的泡沫镍置于丙酮、乙醇溶液中分别超声25-35min，然后浸于浓度为1mol/L的盐酸溶液中刻蚀20-30min，用大量的去离子水洗净后，放于52-58℃的烘箱内干燥，备用；将15-25份醋酸锰和20-30份醋酸铵溶于90-100份蒸馏水中，将泡沫镍置于上述溶液中，在0.7-0.9mA/cm2的电流密度下沉积35-45min，...
【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：启东祥瑞建设有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。