The invention relates to a high hardness and wear-resistant ceramic and its preparation process, including a green body and a glaze; the green body is composed of the following raw materials: 60 to 80 parts clay, 20 to 25 parts quartz, 15 to 20 parts feldspar, 2 to 5 parts sand, and 1 to 4 parts medicine; the glaze is composed of the following raw materials: rutile 50 to 4 parts. To 65, quartz 20 to 25, calcite 5 to 10, fluorite 5 to 9, vegetable ash 5 to 8, zinc oxide 0.5 to 0.8, copper oxide 0.1 to 0.3; the raw materials provided in the invention are reasonable, the raw materials are dispersed evenly, and the bonding strength between the raw materials in the firing process is tightly bonded, which greatly enhances the bonding strength of Jun porcelain. The glaze surface can form a hard wear-resistant layer, the porcelain is not easy to crack, high yield, economic and practical and artistic value.
【技术实现步骤摘要】
一种高硬度耐磨损的陶瓷及其制备工艺
本专利技术属于钧瓷
，具体涉及一种高硬度耐磨损的陶瓷及其制备工艺。
技术介绍
钧瓷，河南省禹州市特产，中国国家地理标志产品。钧瓷始于唐、盛于宋，是中国古代五大名瓷之一，并以其独特的釉料及烧成方法产生的窑变神奇而闻名于世。瓷作为中国陶瓷艺术史上的一个重要符号，在世界陶瓷发展史上占有重要地位。自古就有“黄金有价钧无价”、“家有万贯，不如钧瓷一片”之说。它独特的窑变艺术，以其“入窑一色，出窑万彩”的艺术特点广受陶瓷爱好者喜爱。钧瓷造型古朴端庄，器型规整，胎壁厚薄匀称。制瓷工匠合理地利用各种原料制坯，基本上掌握了原料的烧缩性能，再加上高超的成型工艺，所制器皿规格统一，尺寸一致。原料的使用上，能够合理使用，保证胎釉的烧成温度和膨胀系数的基本一致。釉质玻璃化程度好，促进胎釉间钙长石中间层的形成，使胎釉结合程度高，釉层一般无剥釉现象。釉料配制含磷、钛、铜、锡等元素，为复色窑变花釉的形成提供了内在条件。钧瓷工匠还利用含不同金属氧化物的各种原料，进行多次分层施釉的方法，使产品形成绚丽多彩、自然生动的窑变流纹。陶瓷研究者用仪器观察宋代钧瓷标本...
【技术保护点】
1.一种高硬度耐磨损的陶瓷，其特征在于：包括坯料及釉料；所述的坯料由以下重量份的原料组成：粘土60至80份，石英20至25份，长石15至20份，砂石2至5份，本药1至4份；所述的釉料由以下重量份的原料组成：红长石50至65份，石英20至25份，方解石5至10份，萤石5至9份，草木灰5至8份，氧化锌 0.5至0.8份，氧化铜0.1至0.3份。
【技术特征摘要】
1.一种高硬度耐磨损的陶瓷，其特征在于：包括坯料及釉料；所述的坯料由以下重量份的原料组成：粘土60至80份，石英20至25份，长石15至20份，砂石2至5份，本药1至4份；所述的釉料由以下重量份的原料组成：红长石50至65份，石英20至25份，方解石5至10份，萤石5至9份，草木灰5至8份，氧化锌0.5至0.8份，氧化铜0.1至0.3份。2.根据权利要求1所述的高硬度耐磨损的陶瓷，其特征在于：所述坯料由以下重量份的原料组成：粘土75份，石英22份，长石18份，砂石4份，本药3份。3.根据权利要求1所述的高硬度耐磨损的陶瓷，其特征在于：所述的釉料由以下重量份的原料组成：红长石60份，石英23份，方解石8份，萤石...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。