一种鼓钉洗钧瓷工艺品的制作方法技术

本发明专利技术公开一种鼓钉洗钧瓷工艺品的制作方法，其特征在于：包括以下步骤，步骤1、选取陶土；步骤2、制浆练泥；步骤3、成型；将步骤2的泥块放在拉坯机上，根据预先的设计，用手拉出器型，即为毛坯，在拉坯机上把毛坯旋成厚度合适、造型美观的壳体，旋坯后在坯体上粘接足、鼓钉附件；步骤4、素烧；步骤5、实釉；步骤6、烧制；所述的陶土包括以下组分：高岭土65‑75%，砂石8‑15%，铅粉8‑12%，莫来石8‑10%，铁矿石3‑5%，氧化钴0.2‑0.4%，食用碱0.3‑0.5%；采用本发明专利技术的陶土，钧瓷成品率高。

A method of making porcelain nail craftwork

The invention discloses a manufacturing method of drum nail washing Jun porcelain handicraft, which is characterized by the following steps: selecting pottery clay; making slurry and mud; forming step 3; placing the mud block of step 2 on the blank drawing machine, according to the pre-design, pulling out the blank by hand, that is, turning the blank on the blank drawing machine. The ceramic clay includes the following components: kaolin 65 75%, sand 8 15%, lead powder 8 12%, mullite 8 10%, iron ore 3 5%, cobalt oxide 0.2 0.4%, food. With alkali 0.3, 0.5%, and the clay of the invention, the finished product of Jun porcelain is high.

【技术实现步骤摘要】
一种鼓钉洗钧瓷工艺品的制作方法
本专利技术涉及钧瓷工艺领域，尤其涉及一种鼓钉洗钧瓷工艺品的制作方法。
技术介绍
陶瓷是中华文化的重要组成部分之一，而钧瓷又是中华陶瓷文化中的一颗璀璨明珠。钧瓷发源于东汉，是宋代五大名窑瓷器之一，是传统制瓷工艺中的珍品，以独特的窑变艺术而著称于世，素有“黄金有价钧无价”和“家有万贯，不如钧瓷一片”的美誉。钧瓷被誉为中国“五大名瓷”之首，为我国河南省禹州市的特产，其主要特征为瓷器的颜色复杂化，改变了古代瓷器的单色釉发展脉络，具有“进窑一色，出窑万彩”等独特的特色，是其他陶瓷工艺品无法实现和比拟的。本专利技术根据"钧官窑鼓钉神洗"为专利技术依据，结合仿青铜制作出，壳体周身凸起鼓钉装饰，壳体下部有三足，钧瓷的关键在于瓷釉，瓷釉在进行釉烧后变彩决定着钧瓷的价值，在烧制时，钧瓷在出窑冷却后极易开裂，从而导致珍品率低。
技术实现思路
有鉴于此，本专利技术提供一种鼓钉洗钧瓷工艺品的制作方法，坯釉结合性能好，成品率高。一种鼓钉洗钧瓷工艺品的制作方法，包括以下步骤：步骤1、选取陶土；所述的陶土包括以下组分：高岭土65-75%，砂石8-15%，铅粉8-12%，莫来石8-10%，本文档来自技高网...

【技术保护点】
1.一种鼓钉洗钧瓷工艺品的制作方法，其特征在于：包括以下步骤，步骤1、选取陶土；步骤2、制浆练泥；步骤3、成型；将步骤2的泥块放在拉坯机上，根据预先的设计，用手拉出器型，即为毛坯，在拉坯机上把毛坯旋成厚度合适、造型美观的壳体，旋坯后在坯体上粘接足、鼓钉附件；步骤4、素烧；步骤5、施釉；步骤6、烧制；所述的陶土包括以下组分：高岭土65‑75%，砂石8‑15%，铅粉8‑12%，莫来石8‑10%，铁矿石3‑5%，氧化钴0.2‑0.4%，食用碱0.3‑0.5%。