The invention discloses an aerated expansion geopolymer used for road grouting reinforcement, which comprises the following components: slag powder, fly ash, silica powder, metakaolin, steel slag powder, aluminum powder, water reducer, foam stabilizer, thickener, redispersible emulsion powder, sodium hydroxide, sodium metasilicate, sodium sulfite and water. . The aerated expansive geopolymer for road grouting reinforcement provided by the invention has good late mechanical properties and durability, low density, extremely low thermal conductivity, no shrinkage cracking, and strong durability under various adverse weather conditions. It is a high performance thermal insulation building material without pollution.
【技术实现步骤摘要】
一种道路注浆加固用的加气膨胀型地聚合物
本专利技术涉及一种地聚合物，尤其涉及一种道路注浆加固用的加气膨胀型地聚合物。
技术介绍
地聚合物是一种由AlO4和SiO4四面体结构单元组成三维立体网状结构的无机聚合物，化学式为Mn{-(SiO2)zAlO2}n·wH2O，无定形到半晶态，属于非金属材料。地聚合物材料，具有自身强度高、流动度大、渗透性好、具有良好的施工性和耐久性等特点，但由于碱性激发剂的选择及其矿物材料自身特点，地聚合物材料存在膨胀率低、收缩、密度大等性能缺点。因此，提供一种加气膨胀型地聚合物材料在建筑工程应用领域具有较为广阔的前景。
技术实现思路
本专利技术所要解决的技术问题是提供一种道路注浆加固用的加气膨胀型地聚合物，能够大大改善产品的膨胀性，降低产品的密度，并有效解决产品收缩开裂的问题。本专利技术为解决上述技术问题而采用的技术方案是提供一种道路注浆加固用的加气膨胀型地聚合物，包含如下组分：矿渣微粉、粉煤灰、微硅粉、偏高岭土、钢渣微粉、铝粉、减水剂、稳泡剂、增稠剂、可再分散乳胶粉、水玻璃、氢氧化钠、偏硅酸钠、亚硫酸钠和水。上述的道路注浆加固用的加气膨胀型地聚...
【技术保护点】
1.一种道路注浆加固用的加气膨胀型地聚合物，其特征在于，包含如下组分：矿渣微粉、粉煤灰、微硅粉、偏高岭土、钢渣微粉、铝粉、减水剂、稳泡剂、增稠剂、可再分散乳胶粉、水玻璃、氢氧化钠、偏硅酸钠、亚硫酸钠和水。
【技术特征摘要】
1.一种道路注浆加固用的加气膨胀型地聚合物，其特征在于，包含如下组分：矿渣微粉、粉煤灰、微硅粉、偏高岭土、钢渣微粉、铝粉、减水剂、稳泡剂、增稠剂、可再分散乳胶粉、水玻璃、氢氧化钠、偏硅酸钠、亚硫酸钠和水。2.如权利要求1所述的道路注浆加固用的加气膨胀型地聚合物，其特征在于，各组分按重量份数配比如下：3.如权利要求1所述的道路注浆加固用的加气膨胀型地聚合物，其特征在于，所述矿渣微粉为活性指数95％以上的矿渣微粉；所述粉煤灰为活性指数70％以上的二级粉煤灰或一级粉煤灰；所述微硅粉目数为600～2000目；所述钢渣微粉比表面积为400～800㎡/kg；所述铝粉中位径为30～100μm。4.如权利要求1所述的道路注浆加固用的加气膨胀型地聚合物，其特征在于，所述减水剂为聚羧酸减水剂或萘系减水剂。5.如权利要求1所述的道路注浆加固用的加气膨胀型地聚合物，其特征在于，所述稳泡剂为聚丙烯酰胺、烷基醇酰胺、氧化胺、聚乙烯醇、蛋白、多肽、淀粉或十二烷基二甲基氧化胺。6.如权利要求1所述的道路注浆加固用的加气膨胀型地聚合物，其特征在于，所述增稠剂...