The invention discloses a flame retardant modified co-extruded wood-plastic composite material, which comprises a core layer and a surface layer melted and co-extruded on the surface of the core layer; the core layer comprises the following mass components: high-density polyethylene 25 35 phr, miscellaneous wood powder 60 70 phr, calcium powder 0.1 0.3 phr, compatibilizer 0.02 0.03 phr, lubricant 0.02 0.04 phr, flame retardant. Magnesium hydroxide 0.05 0.08 phr. The surface layer comprises the following mass components: 85 95 phr. of modified polyolefin, 0.1 0.15 phr. of flame retardant Magnesium hydroxide and an appropriate amount of chromophore. In order to improve the compatibility of the flame retardant in the matrix, the flame retardant performance reaches the European standard flame retardant grade B, and the amount of the core flame retardant is small, which has little influence on the core formability and mechanical properties.
【技术实现步骤摘要】
一种阻燃改性共挤木塑复合材料
本专利技术涉及一种阻燃改性共挤木塑复合材料，属于新材料
技术介绍
木塑复合材料的主要原料是塑料和木质纤维，都属于易燃材料，制品的阻燃性能较差，应用存在有一定的安全隐患。特别是应用于室内装饰的木塑制品，其阻燃等级要求更好，因此需要对木塑复合材料进行阻燃改性。
技术实现思路
为实现上述目的，本专利技术提供一种阻燃改性共挤木塑复合材料。本专利技术提供如下技术方案：一种阻燃改性共挤木塑复合材料，其包括芯层以及熔融共挤在芯层外表面的面层。所述芯层包括以下质量组份：高密度聚乙烯25-35份、杂木粉60-70份、钙粉0.1-0.3份、相容剂0.02-0.03份、润滑剂0.02-0.04份、阻燃剂氢氧化镁0.05-0.08份。所述面层包括以下质量组份：改性聚烯烃85-95份、阻燃剂氢氧化镁0.1-0.15份以及适量色母。上述的阻燃改性共挤木塑复合材料的制备方法为：将所述芯层和所述表层分别高温共混造粒，然后采用锥形双螺杆挤出机将所述表层熔融共挤在所述芯层的外表面。本专利技术的有益效果是：本专利技术通过氢氧化镁对芯层和面层分别进行阻燃改性和高温共混...
【技术保护点】
1.一种阻燃改性共挤木塑复合材料，其包括芯层以及熔融共挤在芯层外表面的面层，其特征在于：所述芯层包括以下质量组份：高密度聚乙烯 25‑35份、杂木粉60‑70份、钙粉 0.1‑0.3份、相容剂 0.02‑0.03份、润滑剂 0.02‑0.04份、阻燃剂氢氧化镁 0.05‑0.08份；所述面层包括以下质量组份：改性聚烯烃 85‑95份、阻燃剂氢氧化镁 0.1‑0.15份以及适量色母。
【技术特征摘要】
1.一种阻燃改性共挤木塑复合材料，其包括芯层以及熔融共挤在芯层外表面的面层，其特征在于：所述芯层包括以下质量组份：高密度聚乙烯25-35份、杂木粉60-70份、钙粉0.1-0.3份、相容剂0.02-0.03份、润滑剂0.02-0.04份、阻燃剂氢氧化镁0.05-0.08份；...
【专利技术属性】
技术研发人员：陈福涛，
申请(专利权)人：宣城福美达新材料有限公司，
类型：发明
国别省市：安徽,34