The invention belongs to the field of BOPP film preparation, in particular to a BOPP matting plastic film and a preparation method thereof. The matting plastic woven film is composed of a surface layer, a surface layer and a core layer; a surface layer is composed of the following components by weight fraction: MAT1006 100%; a surface 2 layer is composed of the following components by weight fraction: F03D 97.00%, ABPP905 3%; and a core layer is composed of the following components by weight fraction: main material 100%. The film produced by the three-layer structure co-extrusion and biaxial stretching molding has the advantages of high composite strength, good heat sealing strength, light weight, simple preparation process, no environmental pollution, and can be used for the packaging of food and other products, and has broad market prospects.
【技术实现步骤摘要】
一种BOPP消光塑编膜及其制备方法
本专利技术属于BOPP薄膜制备领域,具体涉及一种BOPP消光塑编膜及其制备方法。
技术介绍
BOPP薄膜专用母料是以聚丙烯树脂和功能性填料为主要原料、通过挤出加工而成的、同时具有塑料和纸特征的多功能性材料。BOPP薄膜是一种环保产品,具有比重轻、强度大、抗撕裂、印刷性好、遮光、抗紫外线、经久耐用、经济环保等特点。塑编膜是一种非常重要的软包装材料,广泛用于与编织袋外部覆膜,可增加产品的牢度和美观度。传统的塑编袋复合一般使用纸质材料代替,其不可回收二次利用,这样不仅会浪费大量的木材资源,同时还加大了用户的使用成本。目前国内BOPP生产厂家生产塑编膜时,复合强度一直没有达到令人满意的目标,因此下游客户使用时就会出现很多的问题。BOPP生产厂家即使采用了大量的工艺配方和参数也没有克服这个问题,产品质量无法满足客户深层次的需求。
技术实现思路
本专利技术的目的在于提供一种BOPP消光塑编膜及其制备方法,其加工工艺简单,降低制造成本;并且生产出的薄膜具有复合强度高、热封强度好、质轻等优点,无环境污染,使用后的塑编膜可全部回收制作其它塑料制品,可 ...
【技术保护点】
1.一种BOPP消光塑编膜,其特征在于:由表层1、表层2和芯层组成;表1层由以下按重量分数计的组分组成:MAT1006 100%;表2层由以下按重量分数计的组分组成:F03D 97.00%,ABPP905 3%;芯层由以下按重量分数计的组分组成:主料100%。
【技术特征摘要】
1.一种BOPP消光塑编膜,其特征在于:由表层1、表层2和芯层组成;表1层由以下按重量分数计的组分组成:MAT1006100%;表2层由以下按重量分数计的组分组成:F03D97.00%,ABPP9053%;芯层由以下按重量分数计的组分组成:主料100%。2.根据权利要求1所述的一种BOPP消光塑编膜,其特征在于:主料由以下按重量分数计的组分组成:F03D35%、1104k65%。3.一种制备如权利要求1所述的一种BOPP消光塑编膜的方法,其特征在于:采用三层结构共挤塑后双向拉伸成型,工艺参数控制如下:主挤出机的温度为247~260℃;辅挤出机Ⅰ的温度为210~250℃,辅挤出机Ⅱ...