The invention relates to a light conveyor belt with polyurethane surface composite Teflon and a preparation method thereof, belonging to the technical field of conveyor belt. From top to bottom, the polyurethane resin layer comprises Teflon film layer, polyurethane resin layer, bottom fabric layer and polyester fabric skeleton in turn; the polyurethane resin layer comprises TPU powder 90 110 phr and stabilizer 7 9 phr by weight; the bottom fabric layer comprises PU adhesive 90 110 phr, lubricant 2 4 phr and network crosslinking agent 4 6 phr. The conveyor belt provided by the invention can achieve the goal of high temperature resistance and anti-adhesion in food processing by checking the polyurethane gum layer on the conveyor belt surface.
【技术实现步骤摘要】
聚氨酯表面复合特氟龙的轻型输送带及其制备方法
本专利技术涉及一种聚氨酯表面复合特氟龙的轻型输送带及其制备方法，属于输送带
技术介绍
轻型输送带是输送带中的精细产品，以棉、聚酰胺（PA）、涤纶等织物作为带芯或骨架材料，以橡胶（包括橡塑）或塑料作为覆盖层（也可无覆盖层带），表面可以是光滑的，也可以有各种图案的深浅花纹或横向型条、挡板和波纹挡边。轻型输送带具有带体轻薄、尺寸稳定性好、精度高、色彩明快、张力高、安全无毒等特点。同时，随着制备技术的发展，可供用户选择的产品种类和性能范围越来越广，可具有防静电、耐腐蚀、阻燃、低噪音等各种特殊性能。根据国家标准GB/T236772009轻型输送带，按轻型输送带的覆盖层的材料类型可将其分为两大类：橡胶型（包括橡塑型）和塑料型（包括聚氯乙烯PVC、热塑性聚氨酯弹性体TPU、聚乙烯PE等）。传统的橡胶输送带由美国杜邦公司专利技术生产并用于各种物品输送，至今已有100多年的历史。基本上以天然橡胶、丁腈橡胶、氯丁橡胶、丁苯橡胶等为主。目前，通过塑料增强橡胶和橡胶增韧塑料等改性原材料的使用，促使以橡胶为主要原料的输送带转向了新型橡...
【技术保护点】
1.聚氨酯表面复合特氟龙的轻型输送带，其特征是：自上至下依次包括特氟龙薄膜层、聚氨酯胶质层、底层织物层和聚酯织物骨架；按重量份计所述聚氨酯胶质层包括TPU粉90‑110份和稳定剂7‑9份；所述底层织物层包括PU胶90‑110份，润滑剂2‑4份和网络交联剂4‑6份。
【技术特征摘要】
1.聚氨酯表面复合特氟龙的轻型输送带，其特征是：自上至下依次包括特氟龙薄膜层、聚氨酯胶质层、底层织物层和聚酯织物骨架；按重量份计所述聚氨酯胶质层包括TPU粉90-110份和稳定剂7-9份；所述底层织物层包括PU胶90-110份，润滑剂2-4份和网络交联剂4-6份。2.如权利要求1所述聚氨酯表面复合特氟龙的轻型输送带，其特征是：所述聚酯织物骨架采用聚酯纤维编织而成，具体通过经线和纬线编织而成。3.如权利要求1所述聚氨酯表面复合特氟龙的轻型输送带，其特征是：所述经线包括第一经线和第二经线，所述第一经线采用单根聚酯纤维构成，所述第二经线采用多根纤维构成，所述第一经线与第二经线间隔设置。4.如权利要求1所述聚氨酯表面复合特氟龙的轻型输送带，其特征是：所述稳定剂具体为钙锌稳定剂。5.如权利要求1所述聚氨酯表面复合特氟龙的轻型输送带，其特征是：所述润滑剂具体为聚乙烯蜡或低分子量聚丙烯。6.如权利要求1所述聚氨酯表面复合特氟龙的轻型输送...
【专利技术属性】
技术研发人员：张建伟，张浩，张华，高洪才，
申请(专利权)人：无锡市顺晟工业制带有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。