The invention belongs to the technical field of organic polymer synthesis, in particular to a waterborne polyurethane ink and a preparation method thereof. Polyurethane latex is prepared by mixing polyurethane latex and color paste at a weight ratio of 3:1. Polyurethane latex is made from the following raw materials: isocyanate, toluene 2,4_diisocyanate, polyether polyol, polyester diol, triethylamine, 1,4_butanediol, dimethylol butyric acid, deionized water, acetone. Colorants are made from the following materials: pigments and deionized water. The waterborne polyurethane ink has the advantages of safety and environmental protection, good stability, fast drying speed, high adhesion, high film forming performance and friction resistance, and the preparation method is also provided, which is easy to industrialize production.
【技术实现步骤摘要】
水性聚氨酯油墨及其制备方法
本专利技术属于有机高分子合成
，具体涉及一种水性聚氨酯油墨及其制备方法。
技术介绍
油墨是用于印刷的重要材料，普通的胶印油墨中都含有矿物油，并且对人体有害。水性油墨不含挥发性有机溶剂，安全、无毒，被大量用于食品、药品、儿童玩具中的软包装印刷。但目前水性聚氨酯油墨存在诸多问题，如：稳定性较差、干燥速度慢、附着力低、成膜性能一般，不能很好满足印刷的要求。
技术实现思路
针对现有技术的不足，本专利技术的目的是提供一种水性聚氨酯油墨，安全环保，稳定性好、干燥速度快、附着力高、成膜性能高，耐摩擦；本专利技术还提供其制备方法。本专利技术所述的水性聚氨酯油墨，由聚氨酯乳胶和色浆按重量比为3:1混合配制而成，聚氨酯乳胶由以下重量份数的原料制成：色浆由以下重量份数的原料制成：颜料10份和去离子水50份。聚醚多元醇的相对分子质量为500-1500，官能度为1.5-2.5。聚酯二元醇的相对分子质量为1000-1500，官能度为1.5-2.5。颜料为酞菁蓝。所述的水性聚氨酯油墨的制备方法：(1)将聚醚多元醇、聚酯二元醇投入反应瓶中，加入异氰酸酯、甲苯-2,4-二异氰酸酯，升温至80℃，反应1小时，降温至50℃，加入二羟甲基丁酸，控制温度80℃条件下，搅拌反应1小时，得到预聚物，加入1,4-丁二醇反应2小时后，冷却至室温，得到预聚体；加入丙酮，搅拌均匀；滴加三乙胺，加入去离子水，乳化，蒸去丙酮，得到聚氨酯乳胶；(2)将颜料和去离子水混合搅拌均匀，得到色浆；(3)将聚氨酯乳胶和色浆混合，50℃搅拌20分钟，冷却得到产品。本专利技术具有以下优点：本专利技术...
【技术保护点】
1.一种水性聚氨酯油墨，其特征在于：由聚氨酯乳胶和色浆按重量比为3:1混合配制而成，聚氨酯乳胶由以下重量份数的原料制成：
【技术特征摘要】
1.一种水性聚氨酯油墨，其特征在于：由聚氨酯乳胶和色浆按重量比为3:1混合配制而成，聚氨酯乳胶由以下重量份数的原料制成：色浆由以下重量份数的原料制成：颜料10份和去离子水50份。2.根据权利要求1所述的水性聚氨酯油墨，其特征在于：聚醚多元醇的相对分子质量为500-1500，官能度为1.5-2.5。3.根据权利要求1所述的水性聚氨酯油墨，其特征在于：聚酯二元醇的相对分子质量为1000-1500，官能度为1.5-2.5。4.根据权利要求1所述的水性聚氨酯油墨，其特征在于：颜料为酞菁蓝。5.一种权...