The invention relates to a composite, a metal powder forming body, a method for manufacturing a sintered body and a sintered body. The composite used for metal powder injection molding is characterized in that it has secondary particles, in which the first metal particles combine with each other, and a matrix region, including a second metal particle and an adhesive, and a second metal particle whose composition material is the same as the first metal particle and the average particle size is smaller. In addition, it is preferable that any of the above-mentioned first metal particles is composed of Fe-based alloy, Ni-based alloy or Co-based alloy. In addition, the above two particles are preferably formed by binding of the first metal particles to each other by binding agents.
【技术实现步骤摘要】
复合物、金属粉末成形体、烧结体的制造方法以及烧结体
本专利技术涉及金属粉末注射成形用复合物、金属粉末成形体、烧结体的制造方法以及烧结体。
技术介绍
作为使金属粉末成形的方法，已知将包含金属粉末和有机粘合剂的造粒粉末填充到规定的成形模具并进行压缩而得到规定形状的成形体的压缩成型法。得到的成形体经除去有机粘合剂的脱脂处理、将金属粉末烧结的烧成(烧制)处理而成为金属烧结体。这种技术是一种粉末冶金技术，能根据成形模具的形状大量制造复杂形状的金属烧结体，所以近年来在许多工业领域中正在普及。例如，在专利文献1中公开了如下金属粉末注射成形法：其中，将金属粉末与粘合剂混合而成的成形材料注射到模具内使成形体成形，接着，加热成形体而除去粘合剂，之后，使成形体烧结。并且，公开了将金属粉末与粘合剂混合而制备复合物时的混合比设为60:40。专利文献1：日本特开2001-152205号公报近年来，针对金属烧结体不仅要求金属材料所特有的高强度，还要求高延展性和高韧性等特性。即，要求实现兼顾有一般存在相反倾向的高强度和高延展性的金属烧结体。但是，现有的金属烧结体无法充分地响应这种市场要求。专利技...
【技术保护点】
1.一种金属粉末注射成形用复合物，其特征在于，具有：二次粒子，在所述二次粒子中，第一金属粒子彼此结合；以及基质区域，包括第二金属粒子和粘合剂，所述第二金属粒子的构成材料与所述第一金属粒子的构成材料相同、且所述第二金属粒子的平均粒径小于所述第一金属粒子的平均粒径。
【技术特征摘要】
2017.02.24 JP 2017-0339161.一种金属粉末注射成形用复合物，其特征在于，具有：二次粒子，在所述二次粒子中，第一金属粒子彼此结合；以及基质区域，包括第二金属粒子和粘合剂，所述第二金属粒子的构成材料与所述第一金属粒子的构成材料相同、且所述第二金属粒子的平均粒径小于所述第一金属粒子的平均粒径。2.根据权利要求1所述的金属粉末注射成形用复合物，其特征在于，所述第一金属粒子的构成材料是Fe基合金、Ni基合金和Co基合金中任一种。3.根据权利要求1或2所述的金属粉末注射成形用复合物，其特征在于，所述二次粒子是所述第一金属粒子彼此经由粘合剂结合而成的。4.根据权利要求1或2所述的金属粉末注射成形用复合物，其特征在于，在所述二次粒子中，所述第一金属粒子相互自粘。5.根据权利要求1至4...
【专利技术属性】
技术研发人员：中村英文，秀嶋保利，
申请(专利权)人：精工爱普生株式会社，
类型：发明
国别省市：日本,JP