The invention relates to a method for manufacturing a clay ashtray box, which comprises three steps of material selection, molding and surface decoration, and is characterized in that: (1) material selection: dry fine clay with moisture content of 7%-19%; and (2) molding: dry fine clay of step (1) is put into a extrusion die and extruded into matching clay ashtray containers and clay respectively by pressing with a press. The outer surface of the ashtray box is decorated by colored painting or colored spraying after removing excess extrusion edges from the clay ashtray box and the clay ashtray box lid formed by extrusion. Compared with the existing technology, this kind of clay ash box is made of dry fine clay and natural resources, so it has low cost and saves wood and stone resources; because it is mold extrusion industrial production, it has high production efficiency.
【技术实现步骤摘要】
一种黏土骨灰盒的制造方法
本专利技术涉及一种骨灰盒的制造方法，具体的说是一种黏土骨灰盒的制造方法。
技术介绍
骨灰盒，是遗体火化后用来装骨灰的盒状容器。目前多为木质或石质，制造时效率低，成本高；目前在农村有入土为安的习俗，所以多数是把骨灰盒埋葬于土中，由于降解慢，残留多，所以易污染土地。
技术实现思路
本专利技术要解决的技术问题是提供一种用黏土为原料制造骨灰盒的方法。本专利技术采取的技术方案是：一种黏土骨灰盒的制造方法，它包括选料，模压成形和表面装饰三个步骤，其特征是：①选料：选取含水份7%—19%的干细黏土；②模压成形：把步骤①的干细黏土放入挤压模具中用压力机加压分别挤压成配套的黏土骨灰盒皿和黏土骨灰盒盖；③把步骤②挤压成形的黏土骨灰盒皿和黏土骨灰盒盖修整去多余的挤出边后对该骨灰盒的外表面进行彩绘装饰或彩色喷涂装饰。采用以上技术方案中的方法制造该种黏土骨灰盒，与现有技术相比，因它的材质是选用干细黏土，是天然资源，所以它成本低，节省木材和石材资源；因它是模具挤压工业化生产，所以它生产效率高；因它的材质是干黏土，埋葬后易水解变回土，所以它取之于土，回归于土，属于自然循环；因它降解快和无残留，所以它不污染土地。附图说明图1是用本专利技术方法生产出的黏土骨灰盒的结构示意图。图中：1、黏土骨灰盒皿；2、黏土骨灰盒盖。具体实施方式在图1中，本专利技术提供的一种黏土骨灰盒的制造方法，它包括选料，模压成形和表面装饰三个步骤，其特征是：①选料：选取含水份7%—19%的干细黏土；②模压成形：把步骤①的干细黏土放入挤压模具中用压力机加压分别挤压成配套的黏土骨灰盒皿（1）和黏土骨灰...
【技术保护点】
1.一种黏土骨灰盒的制造方法，它包括选料，模压成形和表面装饰三个步骤，其特征是：①选料：选取含水份7%—19%的干细黏土；②模压成形：把步骤①的干细黏土放入挤压模具中用压力机加压分别挤压成配套的黏土骨灰盒皿（1）和黏土骨灰盒盖（2）；③把步骤②挤压成形的黏土骨灰盒皿（1）和黏土骨灰盒盖（2）修整去多余的挤出边后对该骨灰盒的外表面进行彩绘装饰或彩色喷涂装饰。
【技术特征摘要】
1.一种黏土骨灰盒的制造方法，它包括选料，模压成形和表面装饰三个步骤，其特征是：①选料：选取含水份7%—19%的干细黏土；②模压成形：把步骤①的干细黏土放入挤压模具中用压力机加压...