一种加钌硬质合金制造技术

本发明专利技术属于硬质合金制备技术领域，具体涉及一种加钌硬质合金，其混合料包括以下质量份数的组分：WC89.5‑91.4份，Co粉8‑10份，所述混合料还包括Ru粉，所述Ru粉重量为Co粉重量的5％‑10％，Ru粉的激光粒度D(0.5)≤3.0μm。本发明专利技术公开的一种加钌硬质合金，其采用高熔点金属钌作为添加剂，通过粉末冶金的方法烧结制成合金，金属钌固溶于粘结相Co中，能有效强化粘结相，从而显著提升硬质合金基体的高温性能。

A ruthenium carbide

The invention belongs to the technical field of cemented carbide preparation, in particular to a ruthenium-added cemented carbide. The mixture comprises the following components of mass fraction: WC89.5_91.4 phr, Co powder 8_10 phr. The mixture also includes Ru powder, the weight of which is 5%10% of the weight of Co powder, and the laser particle size D (0.5) < 3.0 micron of Ru powder. The invention discloses a ruthenium-added cemented carbide, which uses high-melting-point metal ruthenium as additive and is sintered by powder metallurgy. The metal ruthenium solidifies in the bonding phase Co and can effectively strengthen the bonding phase, thereby significantly improving the high-temperature performance of the cemented carbide matrix.

【技术实现步骤摘要】
一种加钌硬质合金
本专利技术属于硬质合金制备
，具体涉及一种加钌硬质合金。
技术介绍
硬质合金作为一种常用的合金材料，其具有独特的性能，如高抗压强度、良好耐磨性、高硬度、高弹性模量、抗冲击强、耐振动性好、耐腐蚀好等。这使得它被广泛地应用于金属切削，非金属切削操作(如矿石，石油，天然气钻削)，交通运输业，建筑，金属成型，结构和流体处理元件，木工工具等领域。目前，硬质合金在金属加工和非金属加工领域的产量相当。粉末冶金技术的应用使得可通过原料的组合制备具有定制性能的硬质合金。众所周知硬质合金最常见的粘接剂是Co，以Co作为粘接剂的硬质合金在室温下具有优异的力学性能，所以机械加工刀具常采用这种材料制成。但是随着刀具在切削加工过程温度的升高，硬质合金Co粘结相在耐高温和抗氧化等方面的弱点就会暴露出来，导致刀具磨损急剧增大；特别是在加工高强度钢这样的材料时，高速加工会导致刀尖刃口产生塑性变形，影响加工质量的同时降低了刀具使用寿命。
技术实现思路
本专利技术的目的是克服现有技术的不足，提供一种加钌硬质合金。为了达到上述目的，本专利技术采用了下列2个技术方案：一种加钌硬质合金，其混合料包括以下质量本文档来自技高网...

【技术保护点】
1.一种加钌硬质合金，其特征在于，其混合料包括以下质量份数的组分：WC                                 89.5‑91.4份，Co粉                               8‑10份，所述混合料还包括Ru粉，所述Ru粉重量为Co粉重量的5％‑10％，Ru粉的激光粒度D(0.5)≤3.0μm。

【技术特征摘要】
1.一种加钌硬质合金，其特征在于，其混合料包括以下质量份数的组分：WC89.5-91.4份，Co粉8-10份，所述混合料还包括Ru粉，所述Ru粉重量为Co粉重量的5％-10％，Ru粉的激光粒度D(...

【专利技术属性】
技术研发人员：杨新宇，张勇，唐启佳，
申请(专利权)人：自贡硬质合金有限责任公司，
类型：发明
国别省市：四川,51