The invention relates to the technical field of coatings, and discloses an environmentally friendly superhydrophobic impact resistant epoxy resin powder coating and a preparation method thereof. The powder coating consists of 70-80 parts of modified phenolic epoxy resin, 20-30 parts of nano-clay, 15-20 parts of carbon black, 10-20 parts of aluminum nitride microparticles, 0.2-0.5 parts of zinc oxide, 0.2-0.5 parts of sodium pentachlorophenol, 0.5-1 parts of 2,4_dihydroxybenzophenone, 1-2 parts of borax and 0.2 parts of p-phenylenediamine. The powder coating has good impact resistance, heat resistance and waterproof performance, and is green and environment-friendly.
【技术实现步骤摘要】
一种环保超疏水抗冲击环氧树脂粉末涂料及其制备方法
本专利技术涉及涂料
，尤其是涉及一种环保超疏水抗冲击环氧树脂粉末涂料及其制备方法。
技术介绍
涂料是一种有颜料或不含颜料的，用树脂及油制成的化工产品。将涂料涂覆在物体表面能够干结成膜，使被涂物质表面与环境介质隔开，从而对被涂物质起到保护的作用。涂料通常包括环氧树脂涂料、氨基树脂涂料、酚醛树脂涂料、醇酸树脂涂料等。其中环氧树脂涂料具有优异的耐化学性能和防腐性能，并且对金属、玻璃、陶瓷等都具有良好的附着力，被广泛应用于钢铁构架、建筑、车辆、家具等的涂装，受室外天气条件的影响，要求涂料具有较好的耐老化、防水、抗冲击等性能以延长涂料的使用寿命。现有环氧树脂涂料中，环氧树脂涂料硬度较大，易碎，防水效果不佳。
技术实现思路
本专利技术是为了克服现有技术环氧树脂易碎、防水效果不佳的问题，提供一种抗冲击防水的环氧树脂粉末涂料。本专利技术还提供了一种环氧树脂粉末涂料的制备方法。为了实现上述目的，本专利技术采用以下技术方案：一种环保超疏水抗冲击环氧树脂粉末涂料，包括以下重量份数配比的原料：改性酚醛环氧树脂70～80份，纳米粘土20～...
【技术保护点】
1.一种环保超疏水抗冲击环氧树脂粉末涂料，其特征在于，包括以下重量份数配比的原料：改性酚醛环氧树脂70~80份，纳米粘土20~30份，炭黑15~20份，氮化铝微米颗粒10~20份，氧化锌0.2~0.5份，五氯酚钠0.2~0.5份，2,4‑二羟基二苯甲酮0.5~1份，硼砂1~2份，对苯二胺0.2~0.5份。
【技术特征摘要】
1.一种环保超疏水抗冲击环氧树脂粉末涂料，其特征在于，包括以下重量份数配比的原料：改性酚醛环氧树脂70~80份，纳米粘土20~30份，炭黑15~20份，氮化铝微米颗粒10~20份，氧化锌0.2~0.5份，五氯酚钠0.2~0.5份，2,4-二羟基二苯甲酮0.5~1份，硼砂1~2份，对苯二胺0.2~0.5份。2.根据权利要求1所述的一种环保超疏水抗冲击环氧树脂粉末涂料，其特征在于，所述改性酚醛环氧树脂的制备方法为：将5~10重量份数的酚醛环氧树脂和150~200重量份数的正丁醇加入到四口烧瓶中，升温至70~80℃，搅拌溶解，然后加入3~6重量份数的巴豆酸、2~5重量份数的乡叶醇、2~5重量份数的γ-甲基丙烯酰氧基丙基三甲氧基硅烷和0.02~0.03重量份数的偶氮二异丁酸二甲酯引发剂，搅拌反应4~6h，使用旋转蒸发仪将正丁醇溶剂蒸馏出，固化后得到改性酚醛环氧树脂。3.根据权利要求1所述的一种环保超疏水抗冲击环氧树脂粉末涂料，其特征在于，所述氮化铝微米颗粒经过预处理，预处理方法为：将2~5重量份数的氮化铝微米颗粒加入30~40重量份数的去离子水中，升温至40~50℃并搅拌2~5h，然后加入0.5~1重量份数的Ti(SO4)2，继续搅拌反应3~4h，过滤后得到的产物放入烘箱中...