The invention provides a cathode active material, a cathode material, a lithium-ion battery and a device and a preparation method thereof, and relates to the technical field of lithium-ion batteries. The cathode active material comprises 532 lithium nickel manganese cobalt oxide and lithium manganate. The cathode material and lithium-ion batteries contain the cathode active material and have safety. The advantages of high and low cost solve the technical problems of the lack of a cathode active material, cathode material, lithium-ion battery and its preparation method which can reduce the cost of lithium-ion battery and improve the safety of lithium-ion battery.
【技术实现步骤摘要】
正极活性材料、正极材料、锂离子电池及其驱动的装置和制备方法
本专利技术涉及锂离子电池领域，尤其是涉及一种正极活性材料、正极材料、锂离子电池及其驱动的装置和制备方法。
技术介绍
锂离子电池是一种二次电池，即充电电池，它主要依靠锂离子在正极和负极之间移动来工作。在充放电过程中，Li+在两个电极之间往返嵌入和脱嵌：充电时，Li+从正极脱嵌，经过电解质嵌入负极，负极处于富锂状态；放电时则相反。电池一般采用含有锂元素的材料作为电极，是现代高性能电池的代表。锂离子电池的正极活性材料通常为锂钴氧化物、锂镍氧化物和锂锰氧化物，其中钴酸锂是目前应用最广的电池材料，但钴资源日益匮乏，价格昂贵，且钴酸锂电池在使用过程中存在安全隐患。因此，一种在降低锂离子电池成本的同时还能提高锂离子电池安全性的正极活性材料是目前市场需要的。有鉴于此，特提出本专利技术。
技术实现思路
本专利技术的第一目的在于提供一种正极活性材料，本专利技术的第二目的在于提供一种包含上述正极活性材料的正极材料，本专利技术的第三目的在于提供一种包含上述正极活性材料或上述正极材料的锂离子电池，本专利技术的第四目的在于提供了一种上述...
【技术保护点】
1.一种正极活性材料，其特征在于，所述正极活性材料包含质量比为5.2:1‑4:6的532型镍锰钴酸锂和锰酸锂，所述质量比优选为8:2‑5:5，进一步优选为6:4；所述532型镍锰钴酸锂的化学式为LiNi0.5Mn0.3Co0.2O2。
【技术特征摘要】
1.一种正极活性材料，其特征在于，所述正极活性材料包含质量比为5.2:1-4:6的532型镍锰钴酸锂和锰酸锂，所述质量比优选为8:2-5:5，进一步优选为6:4；所述532型镍锰钴酸锂的化学式为LiNi0.5Mn0.3Co0.2O2。2.一种正极材料，其特征在于，包含权利要求1所述的正极活性材料。3.根据权利要求2所述的正极材料，其特征在于，所述正极材料还包括正极粘结剂和正极导电剂；优选地，所述正极粘结剂包括PVDF；优选地，所述正极导电剂包括导电碳黑。4.根据权利要求3所述的正极材料，其特征在于，所述正极材料按重量份数计包括正极活性材料90-98份、正极粘结剂0.5-3份和正极导电剂0.5-3份；优选地，所述正极材料按重量份数计包括正极活性材料93-97份、正极粘结剂1-2份和正极导电剂1-2份。5.一种锂离子电池，其特征在于，所述锂离子电池包含权利要求1所述的正极活性材料或权利要求2-4中任一项所述的正极材料。6.根据权利要求5所述的锂离子电池，其特征在于，所述锂离子电池还包括负极材料，所述负极材料包括负极活性材料、负极粘结剂和负极导电剂；优选地，所述负极材料按重量份数计包括负极活性材料92-98份、负极粘结剂0.5-7份和负极导...
【专利技术属性】
技术研发人员：苏凯，乔乔，陆文宁，
申请(专利权)人：北京国能电池科技股份有限公司，
类型：发明
国别省市：北京,11