The invention provides a manufacturing method of a tool with hardly rust and no coloring on the surface. The manufacturing method of the tool includes the following process: the plasma process, the metal substrate with the processed surface is loaded in the vacuum tank to produce the plasma in the vacuum tank, and the metal substrate is equal to the same time when the temperature of the metal substrate is reached to 280 to 325. The processing surface becomes sharp, the tool precursor is obtained, and the oxidation process is made. After the production of the plasma is finished, the vacuum tank is cooled to a specific temperature between 100 and 225 C, and the oxygen containing gas is introduced into the inside of the vacuum tank, thus forming oxidation on the surface of the tool precursor. Film covering.
【技术实现步骤摘要】
刀具的制造方法
本专利技术涉及一种刀具的制造方法。
技术介绍
在专利文献1中记载了如下这样的方法，即，为了提高剃须用的剃刀刃、为了进行试样的观察而将样品切制为较薄的切片刀等刀具的刀尖的锐利性，进行等离子处理。这里，在进行了等离子处理后，刀具的表面有时生锈、发生着色。在该情况下，锈有损商品的美观，毁坏商品价值。于是，需要一种不会生锈、不会发生着色的工艺。作为与此相关的以往方法，有以下这样的提案。例如在专利文献2中记载了如下这样的方法：以800℃～1300℃的温度在氧化气氛下进行加热，在不锈钢的表面析出氧化铝膜，从而防止生锈。另外，例如在专利文献3中记载了如下这样的方法：利用混合有含锂化合物的中性盐的电解液对不锈钢进行电解处理，从而防止生锈。另外，例如在专利文献4中记载了如下这样的方法：一边照射紫外线，一边借助电解液对成为对象的金属与电极之间通以交流电或交直流叠加波形的电流来进行电解处理，从而形成非导体覆膜，提高耐腐蚀性。现有技术文献专利文献专利文献1：日本特许第5924094号公报专利文献2：日本特许第2690792号公报专利文献3：日本特开2013-185256号...
【技术保护点】
1.一种刀具的制造方法，其中，所述刀具的制造方法包括如下工序：等离子体工序，将具有通过加工得到的加工面的金属制基材载置在真空槽内，使所述真空槽内产生等离子体，在使所述金属制基材的温度达到了280℃～325℃的状态下，对所述金属制基材进行等离子处理而使所述加工面变得锐利，获得刀具前驱体；以及氧化工序，在结束了等离子体的产生后，使所述真空槽内降温至100℃～225℃间的特定温度，并向所述真空槽的内部导入含氧气体，从而在所述刀具前驱体的表面形成氧化覆膜。
【技术特征摘要】
2017.01.30 JP 2017-0145781.一种刀具的制造方法，其中，所述刀具的制造方法包括如下工序：等离子体工序，将具有通过加工得到的加工面的金属制基材载置在真空槽内，使所述真空槽内产生等离子体，在使所述金属制基材的温度达到了280℃～325℃的状态下，对所述金...
【专利技术属性】
技术研发人员：土屋贵之，阿列克谢·列姆涅夫，
申请(专利权)人：新明和工业株式会社，
类型：发明
国别省市：日本,JP
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。