The invention discloses a low melting point branched polylactic acid and a preparation method thereof. The reaction system is composed of polylactic acid, Lewis acid and three functional acrylate monomers. The mixture is mixed uniformly in a screw extruder or a mixer, and the combination of Lewis acid and three functionalized acrylate monomers can reduce the crystallinity, produce branching and degradation of polylactic acid. The branched poly (lactic acid) with low molecular weight and low crystallinity was prepared. Due to the decrease of crystallinity, decrease of molecular weight and the structure of molecular chain regularization, the modified polylactic acid has good fluidity at 130 C, and can be used in the melting coating of chemical fertilizer to achieve the purpose of sustained release.
【技术实现步骤摘要】
低熔点支化聚乳酸及其制备方法
本专利技术涉及高分子材料科学
,具体为一种低熔点支化聚乳酸及其制备方法。
技术介绍
聚乳酸是由淀粉发酵的乳酸聚合而成,来源可再生,且聚乳酸属于是一种可完全降解的高分子材料,其降解的最终产物是二氧化碳和水,对环境并无任何污染。故用聚乳酸做为化肥缓释的包覆材料是最佳的选择之一,但聚乳酸熔点较高,在180℃以上方能具备良好的流动性,而尿素、磷酸铵等化肥在140℃以上就要分解,因此熔融包覆难以实现。目前国内外将聚乳酸用于化肥缓释主要是将聚乳酸溶于溶剂,再采取喷涂的方式将聚乳酸涂覆于化肥颗粒表面,该方法的缺点是喷涂后的溶剂处理较为复杂,环境友好性较差。为实现熔融包覆,需要将聚乳酸的熔点大幅降低,使其在130℃以下就要具备良好的流动性,且具有良好的成膜性。
技术实现思路
针对现有技术的不足,本专利技术提供了一种低熔点支化聚乳酸及其制备方法,它使聚乳酸在130℃以下具备了良好的流动性,可用于化肥颗粒表面的熔融包覆,以克服现有技术的不足。为实现以上目的,本专利技术通过以下技术方案予以实现:低熔点支化聚乳酸,按质量份数计算,包括聚乳酸100份、路易斯酸0.5~6份及三官能度丙烯酸酯类单体0.5~5份为制备原料。所述的路易斯酸为氯化镁、氯化铁、氯化钙、氯化铝、氯化锂或氯化锌。所述的三官能度丙烯酸酯类单体为三羟甲基丙烷三丙烯酸酯、乙氧化三羟甲基丙烷三丙烯酸酯、丙氧化甘油三丙烯酸酯或季戊四醇三丙烯酸酯。一种低熔点支化聚乳酸及其制备方法,按上述重量份数取各组分,将所有组分充分混合均匀,在螺杆挤出机或密炼机中熔融共混反应;挤出机温度190~250℃、时 ...
【技术保护点】
1.一种低熔点支化聚乳酸,其特征在于:按质量份数计算,包括聚乳酸100份、路易斯酸0.5~6份及三官能度丙烯酸酯类单体0.5~5份为制备原料。
【技术特征摘要】
1.一种低熔点支化聚乳酸,其特征在于:按质量份数计算,包括聚乳酸100份、路易斯酸0.5~6份及三官能度丙烯酸酯类单体0.5~5份为制备原料。2.根据权利要求1所述的低熔点支化聚乳酸,其特征在于:所述的路易斯酸为氯化镁、氯化铁、氯化钙、氯化铝、氯化锂或氯化锌。3.根据权利要求1所述的低熔点支化聚乳酸,其特征在于:所述的三官能度丙烯酸酯类单体为三羟甲基丙烷三丙烯...