The invention discloses a single tin salt electrolytic coloring additive, including complexing agent, buffer, antioxidant and surface active agent, among which the antioxidants include ferrous sulfate, and the single tin salt electrolytic coloring additive also includes the auxiliary agent of the ferrous sulphate, and the auxiliary agent includes the modified amino amide phosphate zinc. The single tin salt electrolytic coloring additive has good comprehensive performance. It solves the problem that the electrolytic coloring process must have nickel to participate in the reaction, the bath liquid is stable, the color is fast and uniform, the cost can be reduced effectively, and the low carbon energy saving, green environmental protection, and the same process and product quality with the double salt system can be obtained.
【技术实现步骤摘要】
一种单锡盐电解着色添加剂及其应用
本专利技术涉及电解着色添加剂的
，更具体的说是涉及一种单锡盐电解着色添加剂及其应用。
技术介绍
电解着色是铝合金阳极氧化表面处理中常用的工艺。在当前市场上，本领域技术人员多使用双盐着色添加剂，即硫酸镍加硫酸亚锡的体系。在该体系中，硫酸镍有极好的导电性和电流分散性，是电解着色工艺的必备物料。但随着我国对环保的重视，镍盐做为重金属在本
内已被禁用或限用。于是，研究出质量稳定成本低廉而又环保的单锡盐体系(不含硫酸镍)成为本
下一步发展的目标。但是，如果将硫酸镍除去仅使用单锡盐体系会产生底色发生变化、颜色不均匀不稳定的现象，同时会导致分散性差，产生沟槽处颜色明显浅于平面的现象，而且电流的边缘效应会更加明显，亚锡沉积导致“相框”现象严重。由于电流的边角效应，即在工件的边角部电流密度较大，导致边角部位电沉积速度较快，从外观看，工件的上、下、左、右颜色较深，中间颜色较浅，这种现象俗称为“相框”现象。因此在现有技术的背景之下，单锡盐体系由于其着色剂的技术难关尚未攻克，导致投入成本高、运营成本高、生产不稳定、质量不稳定等多种问题，...
【技术保护点】
1.一种单锡盐电解着色添加剂，其特征在于，包括：络合剂、缓冲剂、抗氧化剂、表面活性剂，其中抗氧化剂中包括硫酸亚铁；所述单锡盐电解着色添加剂中还包括所述硫酸亚铁的辅助剂，所述辅助剂包括改性氨基酰胺磷酸锌。
【技术特征摘要】
1.一种单锡盐电解着色添加剂，其特征在于，包括：络合剂、缓冲剂、抗氧化剂、表面活性剂，其中抗氧化剂中包括硫酸亚铁；所述单锡盐电解着色添加剂中还包括所述硫酸亚铁的辅助剂，所述辅助剂包括改性氨基酰胺磷酸锌。2.根据权利要求1所述的一种单锡盐电解着色添加剂，其特征在于，所述络合剂包括酒石酸，所述缓冲剂包括硼酸，所述抗氧化剂还包括硫酸联氨。3.根据权利要求2所述的一种单锡盐电解着色添加剂，其特征在于，所述硫酸联氨的作用还包括与所述酒石酸协同作为络合剂。4.根据权利要求1所述的一种单锡盐电解着色添加剂，其特征在于，所述表面活性剂包括硫脲、聚硫脲或十二烷苯磺酸钠。5.根据权利要求4所述的一种单锡盐电解着色添加剂，其特征在于，按质量份计，所述酒石酸30-40份，所述硼酸10-20份，所述硫酸亚铁25-45份，所述硫酸联氨10-25份，所述改性氨基酰胺磷酸锌1份，所述表面活性剂5-10份。6.根据权利要求5所述的一种单锡盐电解着...