The invention discloses a high strength magnesium lithium alloy containing Er and its preparation method. The magnesium lithium alloy contains components of the following mass percentage: Li 5 ~ 10%, Zn 1 ~ 6%, Er 1 ~ 5%, the allowance is Mg and inevitable impurity. The preparation methods of High Strength Mg Li alloy include three processes: melting, plastic deformation and heat treatment, in which the process of melting process includes: melting, stirring, static heat preservation and casting. The plastic deformation process includes homogenization and plastic deformation, and the heat treatment process includes aging treatment. By adding Zn and Er elements to the magnesium lithium alloy and introducing Mg3Zn6Er as a strengthening phase in the solidification structure of the magnesium lithium alloy, the strength and thermal stability of the Mg Li alloy can be greatly improved. After the subsequent plastic deformation and heat treatment, the magnesium lithium alloy with low density and high strength can be obtained.
【技术实现步骤摘要】
一种含Er的高强度镁锂合金及其制备方法
本专利技术涉及一种金属结构材料领域的镁锂合金及其制备方法，具体地说，涉及一种含Er的高强度镁锂合金及其制备方法。
技术介绍
镁锂合金作为密度最低的金属结构材料，近年来受到越来越多的关注。镁锂合金具有低密度，高比强度和比刚度，良好的电磁屏蔽能力等优点。但是镁锂合金的缺点也很明显。耐蚀性差，经济成本高，绝对强度低限制了镁锂合金的应用。对于镁锂合金强度的提升，常用方法为对合金进行微合金化、热处理和塑性变形。已有报道在镁锂合金中加入Al、Zn、Ag、Si等元素来实现对镁锂合金的微合金化。此外塑性变形也是提高镁锂合金强度的有效方式，塑性变形是晶粒细化，第二相弥散分布，可进一步提高合金强度。周海涛等公开了《一种超轻双相镁锂合金板材的制备工艺》(公开号CN105755410A)，采用LA83-0.4Y铸锭为原材料，先进行均匀化退火处理后，线切割成板坯，板坯通过加热处理后，依次进行多道次热轧处理、去应力退火处理、多道次冷轧处理及去应力退火处理，即可以得到镁锂合金板材。张中武等公开了《一种铒强化镁锂合金及其制备方法》(公开号CN1057554...
【技术保护点】
1.一种含Er的高强度镁锂合金，其特征在于，包括按质量百分数计的如下元素：锂：5～10％、Zn：1～6％、Er：1～5％，余量为镁和不可避免的杂质。
【技术特征摘要】
1.一种含Er的高强度镁锂合金，其特征在于，包括按质量百分数计的如下元素：锂：5～10％、Zn：1～6％、Er：1～5％，余量为镁和不可避免的杂质。2.如权利要求1所述的含Er的高强度镁锂合金，其特征在于，所述杂质的总质量百分数不超过0.02％。3.一种如权利要求1所述的含Er的高强度镁锂合金的制备方法，其特征在于，包括如下步骤：熔炼的步骤、塑性变形的步骤和热处理的步骤。4.如权利要求3所述的含Er的高强度镁锂合金的制备方法，其特征在于，所述熔炼的步骤具体包括如下操作：将合金的各组分配比熔化升温至670～7...
【专利技术属性】
技术研发人员：刘文才，冀浩，吴国华，高占奎，彭翔，魏广玲，丁文江，
申请(专利权)人：上海交通大学，
类型：发明
国别省市：上海,31