The invention relates to a method for synthesizing polyhedral gold palladium alloy nano materials by wet chemical reduction method, which belongs to the field of inorganic chemistry and material synthesis technology. At first, chloroauric acid was dissolved in ultra pure water, and copper acetate solution, eighteen alkyl three methyl ammonium chloride solution and palladium acid solution were added to the solution. After mixing, the fresh ascorbic acid solution was added quickly, and the polyhedron gold nanoparticles palladium alloy nanomaterials were obtained in the constant temperature box of 15 C for 12 hours. The polyhedron like gold palladium alloy nano material prepared by the invention is of uniform size and consists of polyhedron nanoparticles. The advantages of the method are simple operation, low cost, no toxic reagents in the preparation process, and environmental friendliness.
【技术实现步骤摘要】
一种高催化性能多面体状金-钯合金纳米材料的制备方法
本专利技术涉及一种高催化性能多面体状结构的金-钯合金纳米材料的制备方法。
技术介绍
金-钯合金是一种新型的纳米合金材料，同时具有高的催化性能、良好的多面体形貌和强的化学稳定性，广泛应用于气敏、电化学、太阳能电池、传感器等领域。在过去几十年，关于金-钯合金合成的报道有很多，包括湿化学还原法、水热法、电化学法等，成功制备了不同结构和形貌的金-钯合金。其中湿化学还原法具有操作简单，成本低，制备的金-钯合金尺寸形貌可控性好等优点，是制备金-钯合金常用的方法。金-钯合金的性能和其形貌、尺寸、结晶度密切相关，在不同形貌的金-钯合金中，多面体状结构具有大的表面积，电子传输容易，展示出优异的光学、电学和催化特性，引起了大家越来越多的关注与研究。在多面体状的金-钯合金制备过程中，通常会用到有毒试剂，易造成环境污染，无法实现使用无毒无害试剂制备金-钯合金的目的。本专利技术提供了一种制备多面体状的金-钯合金纳米材料的方法，制备过程中使用无毒试剂，可以简单、低廉、环保的制备多面体状的金-钯合金纳米材料，适合于批量生产。
技术实现思路
本专利...
【技术保护点】
1.一种多面体状结构的金‑钯合金纳米材料的制备方法，其特征在于该制备方法包括以下步骤：a. 将氯金酸溶解到超纯水中得到3.0 mL氯金酸溶液；b. 将0.05 mL乙酸铜水溶液，3.0 mL十八烷基三甲基氯化铵的乙二醇溶液和1.0 mL氯钯酸水溶液依次加入到步骤a所得氯金酸水溶液中，搅拌10分钟；c. 待步骤b中溶液充分混合后，迅速加入0.10 mL新鲜制备的抗坏血酸溶液，，轻轻摇动该溶液10分钟；d. 将步骤c所得混合溶液置于15℃恒温箱中反应12小时；e. 反应完毕后，得到产物经离心分离，并用超纯水洗涤，然后放入真空干燥箱中在60℃干燥15 h得到多面体状金‑钯合金纳米材料。
【技术特征摘要】
1.一种多面体状结构的金-钯合金纳米材料的制备方法，其特征在于该制备方法包括以下步骤：a.将氯金酸溶解到超纯水中得到3.0mL氯金酸溶液；b.将0.05mL乙酸铜水溶液，3.0mL十八烷基三甲基氯化铵的乙二醇溶液和1.0mL氯钯酸水溶液依次加入到步骤a所得氯金酸水溶液中，搅拌10分钟；c.待步骤b中溶液充分混合后，迅速加入0.10mL新鲜制备的抗坏血酸溶液，，轻轻摇动该溶液10分钟；d.将步骤c所得混合溶液置于15℃恒温箱中反应12小时；e.反应完毕后，得到产物经离心分...