The invention discloses a graphene / nano silver composite material and its preparation method, mixing the silver nitrate solution with the aqueous solution of graphene oxide and mixing it evenly and slowly adding the bird's nest. After the ultrasonic uniformity, it is placed in the reaction kettle of 160, 220 degrees centigrade, 30 600min. After being removed, the stone is repeatedly cleaned, centrifuged and dried. Silene / nanoscale composites. The invention adopts bird's nest as reducing agent, and the graphene / nano silver composite material is prepared by one-step method, which has the advantages of simple process, mild reaction, and environmental protection.
【技术实现步骤摘要】
一种石墨烯/纳米银复合材料及其制备方法
本专利技术属于纳米材料领域,特别涉及一种石墨烯/纳米银复合材料。
技术介绍
自从2004年英国曼彻斯特大学两位学者发现石墨烯后,由此掀开了石墨烯的研究热潮。石墨烯是由碳原子以sp2杂化轨道形式组成的六角型蜂巢晶格的二维纳米材料,是构成零维富勒烯、一维碳纳米管、三维石墨等碳材料的基本单元。石墨烯是目前世界上最薄的二维材料,拥有极其优异的光、电、力学性能,在光电器件、生物医学材料、吸附材料领域有大量的研究和应用。纳米银具有优良的传热性、导电性、表面活性和催化性能,在光学、催化、微电子、生物传感、抗菌等领域具有巨大的应用价值。石墨烯是单原子厚度的二维石墨碳材料,具有高比表面积、突出的导热性能和力学性能、非凡的电子传递性能等一系列优异性质,是纳米银的理想载体,而存在于石墨烯层间的纳米银粒子可以起到分离邻近石墨烯片层,防止石墨烯发生团聚的作用(何光裕,马凯,侯景会,孙小强,汪信,陈海群.纳米银@石墨烯复合材料的绿色制备及其抑菌性能[J].精细化工,2012,09:840-843;钟涛,杨娟,周亚洲,郑思辉.纳米银-氧化石墨烯复合材料抗菌性能研究进展[J].材料导报,2014,S1:64-66+71;秦静,姜力文,杨春苗,郭贝贝,孙雪菲,王曙光.氧化石墨烯纳米银复合材料的制备及其抗菌性[J].环境化学,2016,03:445-450.)。近年来有不少文献或专利报道了纳米银-石墨烯复合材料的制备和应用,但是它们多采用有毒的水合肼和硼氢化钠作为还原剂。例如Shen利用硼氢化钠和乙二醇的混合还原剂制备了石墨烯−银纳米粒子复合材料(Na ...
【技术保护点】
1.一种石墨烯/纳米银复合材料及其制备方法,其特征在于:将0.01‑100g/L的硝酸银水溶液与0.01‑100g/L的氧化石墨烯水溶液混合搅拌均匀,所述硝酸银与氧化石墨烯的质量比为1:1‑1:10,缓慢加入燕窝,超声均匀后,置于160‑220℃的反应釜中30‑600min,取出后用乙醇反复清洗、离心、干燥处理后得到石墨烯/纳米银复合材料。
【技术特征摘要】
1.一种石墨烯/纳米银复合材料及其制备方法,其特征在于:将0.01-100g/L的硝酸银水溶液与0.01-100g/L的氧化石墨烯水溶液混合搅拌均匀,所述硝酸银与氧化石墨烯的质量比为1:1-1:10,缓慢加入燕窝,超声均匀后,置于160-220℃的反应釜中3...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。