The present invention discloses a flame retardant polyurethane foam material, including A material and B material. The A material includes 25~65 parts of polyether polyol, 10~20 polyol polyol polyol, 7.5 to 25 phr compound flame retardant, 10~25 foamer, 1~3 stabilizer, 0.5 to 2, 3~8 nano silica. The B material includes the following weight components: 60~80 toluene diisocyanate and 20~40 polymethylene polyphenyl isocyanates. The weight ratio of the A material and the B material is (1 to 1.5):1. The flame retardant polyurethane foam material not only has high anti flammability, but also takes into account both mechanical strength and anti aging effect. It has a wider application prospect and can be used in vehicle door, roof and chassis material or building barrier.
【技术实现步骤摘要】
一种阻燃聚氨酯泡沫材料及其制备方法与应用
本专利技术属于材料
，涉及一种阻燃聚氨酯泡沫材料及其制备方法与应用。
技术介绍
聚氨酯泡沫塑料是目前最常用的合成材料之一，具有相对密度小、多孔性、比强度高等特点，根据所用原料及配方的不同可以制成普通软泡、硬泡、高回弹泡沫等。聚氨酯材料因其优异的声学、力学等性能，已经广泛用于保温、隔音和隔热等领域，全球年需求量已经达到500万吨左右，但是聚氨酯泡沫材料在空气中易燃烧，且燃烧时产生大量有毒气体及烟尘。鉴于运输行业、设备及专业场所等方面对所用聚氨酯泡沫材料要求极高，对泡沫材料阻燃安全性提出特殊要求，近年来提高聚氨酯泡沫材料的阻燃性成为未来发展的重要方向。目前，聚氨酯泡沫材料用阻燃剂单一品种众多，用量需求大，为顺应材料的高阻燃、低烟雾、低毒性的形势要求，使用更加高效的阻燃剂，提高聚氨酯泡沫材料的抗燃性能已势不可挡。阻燃剂主要分为三类：含磷和卤素的化合物、含氮化合物、氢氧化物。含磷阻燃剂与含卤素阻燃剂一起使用可以产生协同效应，燃烧时可以生成沉重的三卤化磷、五卤化磷以及卤氧化磷气体，这些不燃气体覆盖在着火物上，起到了隔绝空气的作...
【技术保护点】
1.一种阻燃聚氨酯泡沫材料，其特征在于：包括A料和B料，所述A料包括以下重量份的组分：聚醚多元醇25～65份、聚酯多元醇10～20份、复合阻燃剂7.5～25份、发泡剂10～25份、稳定剂1～3份、催化剂0.5～2份、纳米二氧化硅3～8份；所述B料包括以下重量份的组分：甲苯二异氰酸酯60～80份、多亚甲基多苯基异氰酸酯20～40份。
【技术特征摘要】
1.一种阻燃聚氨酯泡沫材料，其特征在于：包括A料和B料，所述A料包括以下重量份的组分：聚醚多元醇25～65份、聚酯多元醇10～20份、复合阻燃剂7.5～25份、发泡剂10～25份、稳定剂1～3份、催化剂0.5～2份、纳米二氧化硅3～8份；所述B料包括以下重量份的组分：甲苯二异氰酸酯60～80份、多亚甲基多苯基异氰酸酯20～40份。2.根据权利要求1所述的阻燃聚氨酯泡沫材料，其特征在于：所述A料和所述B料的重量比为(1～1.5)：1。3.根据权利要求1所述的阻燃聚氨酯泡沫材料，其特征在于：所述复合阻燃剂包括以下重量份的组分：甲基磷酸二甲酯2.5～10份、四(2-氯乙基)亚乙基二磷酸酯5～15份。4.根据权利要求3所述的阻燃聚氨酯泡沫材料，其特征在于：所述甲基磷酸二甲酯和四(2-氯乙基)亚乙基二磷酸酯的重量比为(0.5～1)：1。5.根据权利要求1所述的阻燃聚氨酯泡沫材料，...
【专利技术属性】
技术研发人员：李祥庆，孙琦，任彬斌，沈凯华，朱鑫，王洪华，朱士洪，李文忠，
申请(专利权)人：江苏向阳科技有限公司，
类型：发明
国别省市：江苏,32