本发明专利技术公开了一种乳制品贴管用热熔胶，涉及胶黏剂技术领域，其采用以下质量分数的原料制作而成：乙烯‑醋酸乙烯酯共聚物（EVA）30~50份，增粘树脂30~60份，粘度调节剂15~30份，抗氧化剂0.5~1.0份。本发明专利技术制备得到的热熔胶，固化速度快、初粘力大、热稳定性优良、无色无味、成本低、适用范围广、低温性能好等特点。

A kind of hot melt adhesive for dairy products

The invention discloses a kind of hot melt adhesive for milk product sticking pipe, which involves the technical field of adhesive, which is made of the raw material of the following mass fraction: ethylene glycol vinyl acetate copolymer (EVA) 30~50 portion, adhesive resin 30~60 portion, viscosity regulator 15~30 portion and antioxidant 0.5~ 1 parts. The hot melt adhesive prepared by the invention has the characteristics of fast curing speed, large initial adhesive force, good thermal stability, colorless and odorless, low cost, wide application range and good low temperature performance.

【技术实现步骤摘要】
一种乳制品贴管用热熔胶
本专利技术专利涉及胶黏剂领域，特别是一种乳制品贴管用热熔胶。
技术介绍
传统的白色贴管用EVA热熔胶，固化速度偏慢，只能满足100~200瓶/小时的线速生产。但随着近几年来我国各大饮料、乳制品生产企业不断引进高速贴管线，平均生产速度都在350瓶/min以上，传统的EVA热熔胶难以满足生产要求。另外，随着乳制品品类，瓶体形状，材质等日益多样化，市面上热熔胶由于对材质的兼容性以及低温效果不足等问题，导致市场上普遍存在低温掉管现象，产品流通到客户端后，严重影响企业品牌形象。因此一款成本适中，固化速度快，低温性能好的贴管用热熔胶的开发将非常具有市场价值。
技术实现思路
针对上述市场现状，本专利技术提供了一种乳制品贴管用热熔胶，其技术方案如下：一种乳制品贴管用热熔胶，其特征在于，包括以下质量份数的成分。一种乳制品贴管用热熔胶，其特征在于：所述乙烯-醋酸乙烯酯共聚物至少包括醋酸乙烯含量20%~33%，熔融指数100~400g/10min之EVA一种或者一种以上。一种乳制品贴管用热熔胶，其特征在于：所述增粘树脂至少包括软化点110~120℃之HC9石油树脂，软化点100~110本文档来自技高网...

【技术保护点】
1.一种乳制品贴管用热熔胶，其特征在于，包括以下质量份数的成分。

【技术特征摘要】
1.一种乳制品贴管用热熔胶，其特征在于，包括以下质量份数的成分。2.根据权利要求书1所述的热熔胶，其特征在于：所述乙烯-醋酸乙烯酯共聚物至少包括醋酸乙烯含量20%~33%，熔融指数100~400g/10min之EVA一种或者一种以上。3.根据权利要求书1所述的热熔胶，其特征在于：所述增粘树脂至少包括软化点110~120℃之HC9石油树脂，软化点100~110℃之HC5石...