The invention relates to a composite foaming agent for concrete, which belongs to the technical field of building materials. The composite foaming agent of the present invention is composed of the following components according to the weight portion: foaming component: 10~15, stabilizer component: 3~5, foam stabilizer: 0.1 ~ 1.5, auxiliary: 0.1 to 3, and the foaming component is a mixture consisting of twelve alkyl benzene sulfonates and twelve alkyl sodium sulfate by mass ratio of 1:1.5 to 2.5. The stabilizing foam component is twelve alkenyl succinamide ammonium acetate, and the foam stabilizer is hydroxymethyl cellulose, and the auxiliary agent is polystyrene. There are also foam and foam stabilizing components in the compound foaming agent, which have good foam stability for the preparation of foamed concrete. The foaming rate of the foaming agent which is only suitable for foam components is increased by 23 ~ 35%.
【技术实现步骤摘要】
一种混凝土复合发泡剂
本专利技术涉及一种混凝土复合发泡剂,属于建筑材料
技术介绍
发泡混凝土,是通过将发泡剂用机械方式充分发泡,并将泡沫与水泥浆均匀混合,然后进行现浇施工或模具成型,经自然养护所形成的一种含有大量封闭气孔的新型轻质保温材料;发泡混凝土是以发泡剂、水泥、粉煤灰、石粉等搅拌成有机胶结料的双套连续结构的聚合物、内含均匀气孔;发泡混凝土是用于屋面保温找坡、地面保温垫层、上翻梁基坑填充,墙体浇注等节能材料。在泡沫混凝土中,气泡通过物理的方式混入混凝土中,在搅拌的过程中混凝土浆料中的砂石等固体颗粒会破坏已成型的气泡,为了保证混凝土内的气泡量为所期待的量,需对气泡进行稳泡处理。
技术实现思路
本专利技术的目的是提供一种复合发泡剂,该复合发泡剂中同时还有发泡和稳泡组分,对发泡混凝土的制备具有很好的稳泡效果。一种混凝土复合发泡剂,所述复合发泡剂按重量份,由下述组分组成:其中,所述发泡组分为由十二烷基苯磺酸钠和十二烷基硫酸钠按质量比为1:1.5~2.5组成的混合物;所述稳泡组分为十二烯基琥珀酰胺乙酸铵;所述稳泡助剂为羟甲基纤维素,所述助剂为聚苯乙烯。进一步地,本专利技术优选所述复合发泡剂按重量份,由下述组分组成:进一步地,所述发泡组分为由十二烷基苯磺酸钠和十二烷基硫酸钠按质量比为1:1.5~2组成的混合物。本专利技术所述混凝土复合发泡剂一个优选的技术方案为:一种混凝土复合发泡剂,所述复合发泡剂按重量份,由下述组分组成:其中,所述发泡组分为由十二烷基苯磺酸钠和十二烷基硫酸钠按质量比为1:1.5~2组成的混合物;所述稳泡组分为十二烯基琥珀酰胺乙酸铵;所述稳泡 ...
【技术保护点】
1.一种混凝土复合发泡剂,其特征在于:所述复合发泡剂按重量份,由下述组分组成:
【技术特征摘要】
1.一种混凝土复合发泡剂,其特征在于:所述复合发泡剂按重量份,由下述组分组成:其中,所述发泡组分为由十二烷基苯磺酸钠和十二烷基硫酸钠按质量比为1:1.5~2.5组成的混合物;所述稳泡组分为十二烯基琥珀酰胺乙酸铵;所述稳泡助剂为羟甲基纤维素,所述助剂为聚苯乙烯。2.根据权利要求1所述的发泡剂,其特征在于:所述复合发泡剂按重量份,...
【专利技术属性】
技术研发人员:麻晔,赵岩,滕丽荣,
申请(专利权)人:大连理工大学,
类型:发明
国别省市:辽宁,21