The invention relates to a environment-friendly engineering plastic for weatherproof pipe, which is prepared from the following components and the raw material of the mass percentage content: high density polyethylene (HDPE) 55, 100, 40, 0, 5, 3, 7, 0, 1. After mixing the above raw materials through a high-speed mixer, the twin screw extruder is used to extrude the wire and the granulator can cut grain. Compared with the existing technology, the material prepared by the invention not only has excellent impact performance, but also has the characteristics of simple process, convenient operation and easy to industrial production, and can be widely used in the field of engineering plastics. One
【技术实现步骤摘要】
一种耐候性管材用环保型工程塑料的制备方法
本专利技术属于高分子材料领域,适用于工程塑料的材料,尤其是涉及一种管材用环保工程塑料。
技术介绍
聚对苯二甲酸乙二醇酯(简称PET)是当今产量最大的热塑性聚酯,主要应用于纺织纤维领域。PET树脂韧性较强,耐摩擦、刚性高、硬度大、尺寸稳定性好、并且具有原料成本低,耐热性好、在较宽的温度范围内能保持优良的物理机械性能,对大多数有机溶剂和无机酸稳定的特点。但由于PET存在抗冲击强度低的缺点,在工程塑料领域应用受限。本专利技术制备一种管材用环保工程塑料,与其相同的配方专利具有更高的抗冲击性能。
技术实现思路
本专利技术的目的就是为了满足塑料材料的市场需求,而提供一种具有高韧性PET合金材料及其制备方法。本专利技术的目的可以通过以下技术方案来实现:一种管材用环保工程塑料由以下组分及质量百分比含量的原料制备得到:高密度聚乙烯(HDPE)55-100份,聚对苯二甲酸乙二醇脂(PET)0-40份,POE0-5份,相容剂3-7份,抗氧剂0-1份;所述的聚对苯二甲酸乙二醇脂(PET)为瓶片回收料,粘度0.7-0.9dl/g所述增韧剂为沈阳科通公司KT系列中的一种或几种。一种管材用环保工程塑料的制备方法采用以下步骤:(1)按照以下组分及质量百分含量配料:高密度聚乙烯(PE)55-100份,聚对苯二甲酸乙二醇脂(PET)0-40份,POE0-5份,相容剂3-7份,抗氧剂0-1份;(2)将上述组分置于在高速混合机中混合1-10分钟,得到预混物;(3)将预混物置于双螺杆挤出机中进行挤出拉丝;(4)将挤出拉的丝送入切粒机进行切割、造粒,即得到一种管 ...
【技术保护点】
1.一种耐候性管材用环保工程塑料,其特征在于,该材料由以下组分及质量百分比含
【技术特征摘要】
1.一种耐候性管材用环保工程塑料,其特征在于,该材料由以下组分及质量百分比含量的原料制备得到:高密度聚乙烯(HDPE)55-100份,聚对苯二甲酸乙二醇脂(PET)0-40份,POE0-5份,相容剂3-7份,抗氧剂0-1份。2.根据权利要求1所述的一种耐候性管材用环保工程塑料,其特征在于,所述的高密度聚乙烯(HDPE)为7042、5300B、5306J、5200B的一种或几种。3.根据权利要求1所述的一种耐候性管材用环保工程塑料,其特征在于,所述相容剂为沈阳科通公司KT系列中的一种或几种。4.根据权利要求1所述的一种耐候性管材用环保工程塑料,其特征在于,所述抗氧剂为1010、3114、DSTP的一种或几种。5.根据权利要求1所述的一种耐候性管材用环保工程塑料,其特征在于,所述聚对苯二甲酸乙二醇脂(PET)为瓶片回收料,粘度0.7-0.9dl/g。6.根据权利要求1所述的一种耐候性管材用环保工程塑料,其特征在于,所述POE为8150、...
【专利技术属性】
技术研发人员:徐哲,李建成,谢众,
申请(专利权)人:黑龙江鑫达企业集团有限公司,
类型:发明
国别省市:黑龙江,23