The invention provides a nickel based active electrode material embedded in ruthenium silicon composite oxide and a preparation method thereof. The embedded material of the active material is ruthenium silicon composite oxide. The average particle size is 12 nm, and the molar ratio of Si to Si+Ru is 0.18 to 0.22: 1. The preparation method of the nickel based active electrode material embedded in the ruthenium and silicon compound oxide is used to deposit the nickel and ruthenium silicon composite oxides at the same time by a composite electroplating method, and the nickel based active electrode material embedded in the ruthenium silicon compound oxide is obtained. The material has excellent hydrogen evolution activity, simple preparation method, strong operability, easy access to raw materials and low cost.
【技术实现步骤摘要】
一种嵌入钌硅复合氧化物的镍基活性电极材料及其制备方法
本专利技术属于应用电化学和能源工业的电极材料领域，具体涉及一种具有高催化性能的电极材料及其制备方法。
技术介绍
1967年含有贵金属氧化物的电极问世后，人们发现这类氧化物具有非常高的电催化活性，因此被称为活性氧化物材料，或简单称为活性材料。最为优越的活性材料是含钌氧化物，大量研究发现，通过掺杂非贵金属元素不仅可以提高含钌阳极材料的综合性能，而且可以明显降低含钌阳极的制作成本，从而使含钌复合氧化物在许多电化学工业中被大量应用。活性阳极的应用，大幅度提高了电极材料的析氯和析氧活性，降低了电耗。相对于阳极材料，对阴极材料的研究较为薄弱，在许多场合仍然采用电催化活性和稳定性较低的镍金属或钛金属作为阴极材料，严重制约了相关电化学工业领域（包括氯碱工业、氯酸盐工业、制药工业和新能源工业等）的发展。20年前，国外专家发现在镍金属中添加活性更高的组元，形成混合物可以使阴极材料的活性显著提高（Ni+RuO2co-depositedelectrodesforhydrogenevolution，《ElectrochemicalAct...
【技术保护点】
一种嵌入钌硅复合氧化物的镍基活性电极材料的制备方法，其特征在于：具体制备步骤如下：1）镍基材处理：采用工业纯镍，镍网或镍板材；经洗涤去脂，在6 M的硫酸水溶液中刻蚀1小时，去离子水冲洗，干燥；2）电镀液配制： 在含有1.2 M 六水合硫酸镍，0.18 M六水合氯化镍，0.45 M 硼酸的电镀液中加入30 g·L
【技术特征摘要】
1.一种嵌入钌硅复合氧化物的镍基活性电极材料的制备方法，其特征在于：具体制备步骤如下：1）镍基材处理：采用工业纯镍，镍网或镍板材；经洗涤去脂，在6M的硫酸水溶液中刻蚀1小时，去离子水冲洗，干燥；2）电镀液配制：在含有1.2M六水合硫酸镍，0.18M六水合氯化镍，0.45M硼酸的电镀液中加入30g·L-1钌硅复合氧化物，其中Si∶Si+Ru摩尔比为0.18～0.22∶1；3)电镀：将步骤（1）得到的镍基材浸入电镀液中，对...
【专利技术属性】
技术研发人员：王欣，唐电，刘雪华，周迎朝，张腾，邹翔达，李国荣，王启凡，唐中帜，周杨杰，
申请(专利权)人：福州大学，
类型：发明
国别省市：福建,35