一种超高居里温度压电陶瓷材料的制备方法技术
A preparation method of ultra-high Curie temperature piezoelectric ceramics
The invention discloses a preparation method of a kind of perovskite structure lanthanum titanate La2Ti2O7 (LTO) piezoelectric ceramic material, which is characterized by the preparation of LTO precursor powder by sol-gel method, and then using the common sintering method to prepare the LTO piezoelectric ceramics. Through the combination of sol-gel method and common sintering method, the preparation technology of LTO ceramics is optimized, which not only reduces the sintering temperature of LTO ceramics, but also improves the electrical properties of LTO ceramics to a certain extent, so that it is expected to play an important role in the field of ultra high temperature.
【技术实现步骤摘要】
一种超高居里温度压电陶瓷材料的制备方法
本专利技术涉及一种超高居里温度类钙钛矿结构钛酸镧La2Ti2O7（LTO）压电陶瓷材料的制备方法，即先用溶胶凝胶法制备LTO前驱粉体，再用普通烧结法在1350~1550℃下烧结6~12小时制成LTO压电陶瓷圆片。本专利技术属于材料科学与工程领域。
技术介绍
高温压电传感技术在化学、材料加工、自动化、航空航天（如喷气式引擎中的电子器件需要承受500~1000℃高温的情况下寿命还需要有100000h以上）以及石油勘探等行业具有重要应用。目前，居里温度Tc大于650℃的材料有LiNbO3(Tc=1150℃)、LiTaO3(Tc=720℃)、Aurivilliusphases（代表为Bi4Ti3O12(Tc=675℃)、类钙钛矿PLS（代表为Sr2Nb2O7(Tc=1342℃)。由于LiNbO3与LiTaO3因为其高温下电导率高，只能在低于300℃使用；Auriviliusphase改进的Bi层状材料也只能在500℃用于压电应用。只有PLS可以在1000℃以上使用，并且可在高真空、强电子轰击环境下使用。但类钙钛矿PLS材料需要在高温...
【技术保护点】
一种类钙钛矿结构钛酸镧La2Ti2O7（LTO）压电陶瓷材料的制备方法，采用以下步骤进行制备：(1) 溶胶凝胶法制备LTO陶瓷前驱粉体将原料按La2Ti2O7的摩尔分数进行配料，采用La(NO3)3、C16H36O4Ti、无水柠檬酸为原料，按照La(NO3)3：C16H36O4Ti：无水柠檬酸=1：0.5~2.5：5~15制备成LTO成溶胶，放入90 ℃的烘箱内烘烤5~10天后获得LTO凝胶，用普通烧结炉在1000~1300 ℃下烧结2~6小时形成LTO前驱体粉末。
【技术特征摘要】
1.一种类钙钛矿结构钛酸镧La2Ti2O7（LTO）压电陶瓷材料的制备方法，采用以下步骤进行制备：(1)溶胶凝胶法制备LTO陶瓷前驱粉体将原料按La2Ti2O7的摩尔分数进行配料，采用La(NO3)3、C16H36O4Ti、无水柠檬酸为原料，按照La(NO3)3：C16H36O4Ti：无水柠檬酸=1：0.5~2.5：5~15制备成LTO成溶胶，放入90℃的烘箱内烘烤5~10天后获得LTO凝胶，用普通烧结炉在1000~1300℃下烧结2~6小时形成LTO前驱体粉末。2.(2)造粒压片在上述烘干的粉体中加入浓度为5~10wt%的聚乙烯醇溶液充分混合后进行造粒，然后在压强为16~20MPa下压制...
【专利技术属性】
技术研发人员：朱建国，李曰毅，包绍明，
申请(专利权)人：四川大学，
类型：发明
国别省市：四川,51