The invention relates to the field of magnesium alloy, in particular to a molybdenum re containing rare earth magnesium alloy and a preparation method thereof. The rare earth magnesium alloy containing molybdenum rhenium contains 52 75wt%Mg, 15 32wt%Mo, 2 6.5wt% rare earth elements, 2 6.5wt%Ca, 0.02 1wt%Re, and the other elements such as Fe, Ni, Si, C, N and other impurities. The preparation method comprises the following steps: (1) smelting, (2) high temperature solid solution treatment, (3) plastic deformation, and (4) destress annealing heat treatment. It is difficult to improve the high temperature mechanical properties of rare earth magnesium alloys, and the addition of molybdenum and rhenium can also reduce the addition of rare earth metals from 10% to less than 6.5%, which can significantly reduce the manufacturing cost of the materials.
【技术实现步骤摘要】
一种含钼铼稀土镁合金及其制备方法
本专利技术涉及镁合金领域，具体涉及一种含钼铼稀土镁合金及其制备方法。
技术介绍
镁合金作为最轻的金属结构材料，具有比强度/比刚度高、尺寸稳定、导热导电性好、资源丰富、容易再回收等优点，因此被誉为“21世纪绿色工程材料”，在航空、航天、电动汽车、高速轨道交通等领域具有广阔的应用前景。但是，镁合金常常由于强度低、耐蚀性和耐热性差等原因严重限制了镁合金在生产生活中的广泛应用。因此，提高镁合金的强度和耐热性是发展镁合金材料的重要课题。稀土镁合金是指含有稀土元素的镁合金，由于大部分稀土元素与镁的原子尺寸半径相差在±15％范围内，在镁中有较大固溶度，因而具有良好的固溶强化和沉淀强化的作用，可以有效地改善合金组织和微观结构，增强合金耐蚀性和耐热性，提高合金室温及高温的力学性能。同时稀土元素原子扩散能力差，对提高镁合金再结晶温度和减缓再结晶过程有显著作用。此外，稀土元素还有很好的时效强化作用，可以析出非常稳定的弥散相粒子，从而大幅度提高镁合金的高温强度和蠕变抗力。目前，在所有合金元素中，稀土(RE)是提高镁合金耐热性能最有效的合金元素，稀土元素在...
【技术保护点】
一种含钼铼稀土镁合金，其特征在于：所述合金中含有52‑75wt％Mg，15‑32wt％Mo，2‑6.5wt％稀土元素，2‑6.5wt％Ca，0.02‑1wt％Re，其余为Fe、Ni、Si、C、N等杂质元素。
【技术特征摘要】
1.一种含钼铼稀土镁合金，其特征在于：所述合金中含有52-75wt％Mg，15-32wt％Mo，2-6.5wt％稀土元素，2-6.5wt％Ca，0.02-1wt％Re，其余为Fe、Ni、Si、C、N等杂质元素。2.根据权利要求1所述的含钼铼稀土镁合金，其特征在于，所述的稀土元素为Ce、La、Ir中的一种或几种。3.根据权利要求2所述的含钼铼稀土镁合金，其特征在于，当所述稀土元素为两种时，两种稀土元素按重量比为1∶1～8。4.根据权利要求2所述的含钼铼稀土镁合金，其特征在于，当所述稀土元素为三种时，三种稀土元素之间的重量比在1∶1∶1～8。5.根据权利要求1-4中所述任何一种含钼铼稀土镁合金的制备方法，其特征在于，包括以下步骤：(1)熔炼：在惰性气体保护下，真空度为0.1M...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。