The invention discloses a kind of wear-resistant nano composite rubber, which uses three ethylene propylene rubber raw rubber, hyperbranched phosphorous amide modified SBA 15 nanomaterials, turpentine, Zinc Oxide, carbon black and N benzoate beta naphthalamides as the main raw material, and the rubber contains hyperbranched phosphorous amide modified SBA 15 nanomaterials, due to hyperbranched PHOSPHOROYL The amines modified SBA 15 nanomaterials have high surface activity and flame retardancy, which make the hyperbranched phosphoramide modified SBA nano materials have high dispersion, flame retardancy and surface tension, and thus make the modified nano composite rubber have high wear resistance.
【技术实现步骤摘要】
一种耐磨型纳米复合橡胶
本专利技术涉及一种耐磨型纳米复合橡胶,属于高分子材料领域。
技术介绍
橡胶长时间在恶劣环境下作用下，分子链会被破坏或进一步交联，从而发生脆化或软化现象，由此耐摩擦橡胶已经被广泛用于各行各业，如三元乙丙橡胶，因其主链由化学性较稳定的饱和烃组成，只在侧链中含有不饱和双键，故其具有优异的耐高温、耐摩擦和耐老化等性能，可广泛用于汽车部件、电线电缆保护套和密封件等领域。众所周知，橡胶是经硫化后才具有宝贵的使用价值，因此在橡胶配方中合适的硫化配合剂可以使橡胶的一系列物理机械性能有较大改善，现有耐磨橡胶硫化剂在提升橡胶的力学性能、耐高温性能、耐老化性能和减小压缩永久变形量方面仍然存在不足，需要进一步提高从而增加耐磨橡胶的使用寿命。
技术实现思路
本专利技术的目的在于提供一种耐磨型纳米复合橡胶，使用该专利技术制备的橡胶耐磨性大幅提高。一种耐磨型纳米复合橡胶，该方法包括以下步骤：步骤1、将100份三元乙丙橡胶生胶、25份超支化磷酰胺改性SBA-15纳米材料、15份松节油、6份氧化锌、40份炭黑和1.5份N-苯基-β-萘胺混合，并在温度为60℃、辊间距为2mm条件...
【技术保护点】
一种耐磨型纳米复合橡胶，其特征在于，其制备方法包括以下步骤：步骤1、将100份三元乙丙橡胶生胶、25份超支化磷酰胺改性SBA‑15纳米材料、15份松节油、6份氧化锌、40份炭黑和1.5份N‑苯基‑β‑萘胺混合，并在温度为60℃、辊间距为2mm条件下混炼，得到改性三元乙丙橡胶母胶；步骤2、将改性三元乙丙橡胶母胶停放8h后与15份硫磺、3份过氧化二异丙苯混合，并在室温条件下再次混炼得到改性三元乙丙橡胶混炼胶；步骤3、改性三元乙丙橡胶混炼胶停放24h后，使用硫化仪测定改性三元乙丙橡胶混炼胶在温度为170℃下的正硫化时间，确定正硫化时间后，混炼胶在温度为170℃、压力为2MPa的条...
【技术特征摘要】
1.一种耐磨型纳米复合橡胶，其特征在于，其制备方法包括以下步骤：步骤1、将100份三元乙丙橡胶生胶、25份超支化磷酰胺改性SBA-15纳米材料、15份松节油、6份氧化锌、40份炭黑和1.5份N-苯基-β-萘胺混合，并在温度为60℃、辊间距为2mm条件下混炼，得到改性三元乙丙橡胶母胶；步骤2、将改性三元乙丙橡胶母胶停放8h后与15份硫磺、3份过氧化二异丙苯混合，并在室温条件下再次混炼得到改性三元乙丙橡胶混炼胶；步骤3、改性三元乙丙橡胶混炼胶停放24h后，使用硫化仪测定改性三元乙丙橡胶混炼胶在温度为170℃下的正硫化时间，确定正硫化时间后，混炼胶在温度为170℃、压力为2MPa的条件下进行硫化，得到耐磨型纳米复合橡胶。2.权利要求1所...