一种苯乙酰化醋酸纤维素有序多孔膜材料及其制备方法技术

本发明专利技术涉及一种苯乙酰化醋酸纤维素有序多孔膜材料及其制备方法。所述的材料是苯乙酰化醋酸纤维素，该材料在高湿度条件下能够高效简便形成有序多孔结构，具有易形成有序多孔膜的特性。而且，本发明专利技术的苯乙酰化醋酸纤维素有序多孔膜材料具有来源丰富、环境友好、无污染，膜材料制备方法简单、多孔膜制备方法简便、多孔膜有序度高等特点，可满足不同领域应用的需要。

Benzene acetylated cellulose acetate ordered porous membrane material and preparation method thereof

The invention relates to a benzene acetylated cellulose acetate ordered porous membrane material and a preparation method thereof. The material described in this paper is benzylated cellulose acetate, which is highly efficient and simple to form an ordered porous structure under high humidity conditions, and is easy to form an ordered porous membrane. Moreover, the ordered porous membrane material of benzylated cellulose acetate has the characteristics of rich source, friendly environment, no pollution, simple preparation method of membrane material, simple preparation method of porous membrane and high order degree of porous membrane, which can meet the needs of different fields of application.

【技术实现步骤摘要】
一种苯乙酰化醋酸纤维素有序多孔膜材料及其制备方法
本专利技术涉及一种纤维素衍生物有序多孔膜材料及其制备方法。
技术介绍
具有微纳米结构的聚合物薄膜在生物材料、光电材料等方面都具有很重要的应用价值，从而得到广泛研究与应用。过去，制备具有微纳米结构的薄膜可以采用不同的模板方法，比如胶体晶、乳液液滴、生物细菌以及过滤膜等模板，但由于其制备过程复杂、模板尺寸固定、模板制备困难等原因，因此很难得到具有可调尺寸或者单分散结构的薄膜。近年来，WidawskiG..RawisoM.andFrancoisB.报道的在高湿度条件下制备具有微观结构薄膜的新方法【Self-OrganizedHoneycombMorphologyofStar-PolymerPolystyreneFilms.Nature369,387~389(1994)】得到逐渐发展，并且因其简单可控，越来越受到人们的关注【Breathfiguresasadynamictemplatingmethodforpolymersandnanomaterials.AdvancedMaterials18,973~989(2006)】。通过这种方法，可以本文档来自技高网...

【技术保护点】
一种苯乙酰化醋酸纤维素有序多孔膜材料，其特征是，所述材料是苯乙酰化醋酸纤维素，其结构式为：

【技术特征摘要】
1.一种苯乙酰化醋酸纤维素有序多孔膜材料，其特征是，所述材料是苯乙酰化醋酸纤维素，其结构式为：其中：R1为CH3CO；R2为CH3CO、C6H5CH2CO或H；在R1和R2的三个取代基中，优选的CH3CO、C6H5CH2CO和H三种不同取代基的取代度为：CH3CO的取代度大于或等于2，C6H5CH2CO的取代度等于或大于0.1，H的取代度小于或等于0.4。2.根据权利要求1所述的苯乙酰化醋酸纤维素有序多孔膜材料，其特征是，该材料的制备方法包括以下步骤：在25~50摄氏度下，在四氢呋喃中溶解醋酸纤维素，加入吡啶、三乙胺缚酸剂，在冰水浴下与苯乙酰卤的...

【专利技术属性】
技术研发人员：刘文勇，周志涵，钟环宇，王志杰，刘家豪，杨明明，王启起，戴炳丰，廖文琦，
申请(专利权)人：湖南工业大学，
类型：发明
国别省市：湖南,43