The present invention relates to a synergistic flame retardant sponge. The synergistic flame retardant sponge is composed of 100 components of polyether polyol, 45 phr diisocyanate diisocyanate, 25 melamine 15, three (B chloro isopropyl) phosphate 5 10, and 5 phosphate and halogen mixed flame retardant 10 copies. The catalyst consists of 0.2, 0.5, 0.5, 2 and 3 4, respectively, wherein the composite catalyst is a combination of amine catalyst and tin catalyst. The invention has the advantages that the invention can improve the flame retardancy of the sponge products and reduce the effects of the flame retardants on the physical properties of the sponges by adjusting the synergistic effects of the formula and the ratio of different proportions of various kinds of flame retardants.
【技术实现步骤摘要】
一种协同型阻燃海绵
本专利技术属于海绵制备
，特别涉及一种协同型阻燃海绵。
技术介绍
随着人们生活水平的提高，海绵制品已经逐渐走进人们的日常，成为不可缺少的一部分。然而由于现行的海绵存在极高的可燃性，使得在海绵的使用过程中存在着较高的安全隐患。传统的阻燃海绵，通过大量采用含卤聚合物或含卤阻燃剂组合而成的阻燃混合物来提高海绵的阻燃性能。然而一旦发生火灾，由于热分解和燃烧，产生大量的烟雾以及有毒的腐蚀性气体，从而增加救灾人员救援难度，因此，低烟低毒也是阻燃材料的必不可少的指标。在不影响到海绵制品的机械性能的条件下，阻燃材料的开发研究是阻燃海绵最需要解决的问题之一。
技术实现思路
本专利技术要解决的技术问题是提供一种能够提高海绵制品的阻燃性能以及降低阻燃剂对海绵制品的各项物理性能的影响的协同型阻燃海绵。为解决上述技术问题，本专利技术的技术方案为：一种协同型阻燃海绵，其创新点在于：所述协同型阻燃海绵是由以下重量份的组分组成：以聚醚多元醇100份计，二甲苯二异氰酸酯40-45份，三聚氰胺15-25份，三（B-氯异丙基）磷酸酯5-10份，磷酸酯与卤素混合阻燃剂5-10份，复...
【技术保护点】
一种协同型阻燃海绵，其特征在于：所述协同型阻燃海绵是由以下重量份的组分组成：以聚醚多元醇100份计，二甲苯二异氰酸酯40‑45份，三聚氰胺15‑25份，三（B‑氯异丙基）磷酸酯5‑10份，磷酸酯与卤素混合阻燃剂5‑10份，复合催化剂0.2‑0.5份，均泡剂0.5‑2份和水3‑4份；其中，所述复合催化剂为胺类催化剂与锡类催化剂的复合，且胺类催化剂与锡类催化剂的质量比为14:5。
【技术特征摘要】
1.一种协同型阻燃海绵，其特征在于：所述协同型阻燃海绵是由以下重量份的组分组成：以聚醚多元醇100份计，二甲苯二异氰酸酯40-45份，三聚氰胺15-25份，三（B-氯异丙基）磷酸酯5-10份，磷酸酯与卤素混合阻燃剂5-10份，复合催化剂0.2-0.5份，均泡剂0.5-2份和水3-4份；其中，所述复合催化剂为胺类催化剂与锡类催化剂的复合，且胺类催化剂与锡类催化剂的质量比为14:5。2.根据权利要求1所述的协同型阻燃海绵，其特征在于：所述聚醚多元醇选用分子量为3000的聚醚多元醇。3.根据权利要求1所述的协同型阻燃海绵，其特征在于：所述二甲苯二异氰酸酯选用异氰酸指数为110-115的二甲苯二异氰酸酯。4.根据权...
【专利技术属性】
技术研发人员：倪张根，林涛，
申请(专利权)人：梦百合家居科技股份有限公司，
类型：发明
国别省市：江苏,32