The invention discloses a preparation method of zinc molybdate, including the following steps: adding the mass of Zinc Oxide and molybdenum trioxide into a reaction kettle with stirred and pinch sleeves, and adding 3 water of 4 times the total mass of material, stirring and beating, at the same time heating up to 60 70 degrees C, adding calcium carbonate or talcum powder, continue After stirring 1H and filtering with a filter press, the filter cake was fed into the drying equipment at 100 and 120 degrees centigrade. After crushing to 20 40cm, the calciner was calcined at 500 and 600 centigrade for 12 hours. The material was cooled to 60, 80 and 80, and then crushed to 100 mesh screens, that is, the invention is made of molybdenum trioxide and Zinc Oxide as raw materials. The preparation of zinc molybdate and then sintering at high temperature makes the hydrolysability of the products greatly reduced, and the whole production process is simple, the investment is small, the process is easy to control, and it has very high economic benefit.
【技术实现步骤摘要】
一种钼酸锌的制备方法
本专利技术涉及防锈颜料
，具体是一种钼酸锌的制备方法。
技术介绍
钼酸锌是一种白色无毒的防锈颜料，由于其安全无毒性，在大力提倡环保的今天，尤其受到各个行业的亲睐，市场前景广阔。目前生产钼酸锌的方法主要是结晶法，虽然用作防锈颜料也可以，但是由于水解度高，并且制备价格高昂，很难推广应用，因此，目前的白色颜料还是以钼酸锌为主，再加入一些碳酸钙或沉淀硫酸钡、滑石粉、二氧化硅等原料，制成白色钼酸盐复合型的防锈颜料，释放钼离子，吸附钢铁表面的亚铁离子形成复合型化合物，在大气中氧气的作用下，使亚铁离子转变为高铁离子，从而组织钢铁的进一步锈蚀。由于水解度的原因，在调制复合型防锈颜料时，钼酸锌的含量往往难以控制，使颜料调配难度增加，因此，研发一种能够降低钼酸锌水解度的制备方法来生产一种水解度较低的钼酸锌，是目前急需解决的问题。
技术实现思路
本专利技术的目的就是针对生产钼酸锌的方法均是采用结晶法，得到的钼酸锌产品水解度高，在颜料调配时难度较大，产品稳定性下降的问题，提供一种钼酸锌的制备方法。本专利技术的一种钼酸锌的制备方法，包括下述步骤：将氧化锌和三氧化钼等...
【技术保护点】
一种钼酸锌的制备方法，其特征在于包括下述步骤：将氧化锌和三氧化钼等摩尔质量加入带搅拌及夹套的反应釜中，然后加入氧化锌和三氧化钼总质量3‑4倍的水，开始搅拌并进行打浆，同时升温至60‑70℃，再加入碳酸钙或滑石粉，加完继续搅拌1h，用压滤机过滤，所得滤饼送入干燥设备在100‑120℃下烘干，破碎至20‑40cm的块料后，送至煅烧炉在500‑600℃下煅烧8‑12小时，将物料冷却至60‑80℃后粉碎，过100目筛包装，即得。
【技术特征摘要】
1.一种钼酸锌的制备方法，其特征在于包括下述步骤：将氧化锌和三氧化钼等摩尔质量加入带搅拌及夹套的反应釜中，然后加入氧化锌和三氧化钼总质量3-4倍的水，开始搅拌并进行打浆，同时升温至60-70℃，再加入碳酸钙或滑石粉，加完继续搅拌1h，用压滤机过滤，所得滤饼送入干燥设备在100-120℃下烘干，破碎至20-40cm的块料...