The invention discloses a simple processing method of metal wire. The process includes: horizontal continuous casting, cold rolling, low oxygen annealing, pull planing, low oxygen annealing, thin acid washing, multi mode stretching, bright annealing, and inspection package, continuous casting temperature of L200 C ~1250 C, continuous casting speed of 1.1~1.8 M / clock, and diluted sulfuric acid with concentration of 5~20% in acid washing. The solution was pickled at 50~85 C and annealed with nitrogen as protective gas. The annealing temperature was 390~410 C and the holding time was 100~150 minutes. The beneficial effect of the invention is: the production process of brass wire provided by the invention has the advantages of high strength, corrosion resistance, easy cutting, good mechanical property, relatively simple process, easy control of the process, low production cost and high production efficiency.
【技术实现步骤摘要】
一种金属线材简易加工方法
本专利技术涉及金属线材加工领域，尤其涉及一种金属线材简易加工方法。
技术介绍
金属合金线材的主要应用领域为拉链制造业、气门芯、条帽线制造业、焊料制造业、眼镜框制造业、接插件制造业、饰件、按纽、钟表制造业及汽车制造业等。铜线材具有高强、耐蚀、易切削和低成本等特点，主要应用于制造各种建筑配件、制锁、接插件、端子、镜架、拉链、条帽和弹簧等领域，其发展方向是充分利用合金的各种边角余料，在铜线中加入铬元素，生产低成本、易切削、高性能的铜线和型线。
技术实现思路
本专利技术的目的是克服现有技术的不足而提供的一种操作方便的金属线材简易加工方法。本专利技术采用的技术方案是：一种金属线材简易加工方法，工艺流程包括：水平连铸→冷轧→低氧退火→拉刨→低氧退火→稀酸洗→多模拉伸→光亮退火→检验包装；连铸温度l200℃～1250℃，连铸速度1.1～1.8米／分钟，酸洗采用浓度为5～20％的稀硫酸溶液，酸洗温度50～85℃，退火加入氮气作保护气，退火温度390～410℃，保温时间100～150分钟。作为本专利技术的进一步改进，清洗步骤，以水分清除黏在线材表面的杂质。作为本专利技术的进一步改进，干燥步骤，对清洗后的线材进行吹气，对线材进行干燥。作为本专利技术的进一步改进，润滑步骤，将润滑介质涂抹于线材表面。本专利技术的有益效果是：本专利技术提供的金属线材生产工艺，其有益效果在于，产品强度高、耐腐蚀、易切削、机械性能好，工艺相对简单，流程易于控制，生产成本低，生产效率高。具体实施方式下面对本专利技术做进一步的说明。实施例１：一种金属线材简易加工方法，工艺流程包括：水...
【技术保护点】
一种金属线材简易加工方法，其特征在于，工艺流程包括：水平连铸→冷轧→低氧退火→ 拉刨→低氧退火→稀酸洗→多模拉伸→光亮退火→检验包装；连铸温度 l200℃～1250℃， 连铸速度 1.1 ～ 1.8米／分钟，酸洗采用浓度为 5 ～ 20％的稀硫酸溶液，酸洗温度50 ～ 85℃，退火加入氮气作保护气，退火温度 390 ～ 410℃，保温时间 100～ 150 分钟。
【技术特征摘要】
1.一种金属线材简易加工方法，其特征在于，工艺流程包括：水平连铸→冷轧→低氧退火→拉刨→低氧退火→稀酸洗→多模拉伸→光亮退火→检验包装；连铸温度l200℃～1250℃，连铸速度1.1～1.8米／分钟，酸洗采用浓度为5～20％的稀硫酸溶液，酸洗温度50～85℃，退火加入氮...