一种花纹陶瓷砖制造技术

本发明专利技术公开了一种花纹陶瓷砖。本发明专利技术的陶瓷砖是由坯料和釉料加工而，其釉料由如下重量配比的基本组分配制而成：氧化钙5‑10份、碳酸氢钠5‑10份、云母粉10‑30份、氧化锂10‑30份、氧化镁5‑15份、氧化铝5‑15份、颜料10‑20份、膨润土20‑50份、复合触变剂0‑3份、分散剂0‑3份、增稠剂0‑3份。本发明专利技术的花纹陶瓷砖，具有不着人工痕迹的自然连续的凹凸纹理装饰效果，具有很强的实用性的同时，由于其应用范围广泛，可以在多个领域使用。

A kind of decorative ceramic tile

The invention discloses a kind of decorative ceramic tile. The ceramic tile of the invention is processed by the blank and the glaze, and the glaze is made up of the basic group of weight ratio as follows: 5 calcium oxide, 5 sodium bicarbonate, 30 sodium bicarbonate, 30 portions of mica powder 10, 10 lithium oxide 30, 5 Magnesium Oxide 5, 5 aluminum oxide 15, pigment 10 20, bentonite and compound thixotropy. 0, 3, 0, 3, thickener 0, 3, respectively. The decorative ceramic tile of the invention has the natural and continuous concave and convex texture decoration effect without artificial trace. It has strong practicability and can be used in many fields because of its wide application range.

【技术实现步骤摘要】
一种花纹陶瓷砖
本专利技术涉及陶瓷加工领域，具体涉及一种花纹陶瓷砖。
技术介绍
目前，在陶瓷墙地砖生产过程中，仿天然石材纹理的瓷砖逐渐成为主流，也越来越得到消费者的推崇。而呈现天然石材纹理的常用方法有两种，它们分别是丝网印刷和格栅条纹布料法。其中丝网印刷方法存在着较大缺陷，其形成的纹理线条与天然石材的纹理线条相比，存在着线条过粗、死板、仿真性差的缺陷。同时，丝网印刷还存在色彩极为有限，发色不够鲜艳的不足。而格栅条纹布料方法也只能制造出一些粗糙、粗犷的纹理线条，此类纹理受布料栅格的限制，单调的只能呈现相同于栅格概约式的图案，无法呈现天然石材纹理线条细腻感以及层次效果。
技术实现思路
针对上述问题，本专利技术提供一种花纹陶瓷砖。本专利技术的目的采用以下技术方案来实现：一种花纹陶瓷砖，由坯料和釉料加工而成，所述釉料由如下重量配比的基本组分配制而成：氧化钙5-10份、碳酸氢钠5-10份、云母粉10-30份、氧化锂10-30份、、氧化镁5-15份、氧化铝5-15份、颜料10-20份、膨润土20-50份、复合触变剂0-3份、分散剂0-3份、增稠剂0-3份。优选的，所述氧化铝为10份。优选的，所述颜料本文档来自技高网...

【技术保护点】
一种花纹陶瓷砖，由坯料和釉料加工而成，其特征在于，所述釉料由如下重量配比的基本组分配制而成：氧化钙5‑10份、碳酸氢钠5‑10份、云母粉10‑30份、氧化锂10‑30份、、氧化镁5‑15份、氧化铝5‑15份、颜料10‑20份、膨润土20‑50份、复合触变剂0‑3份、分散剂0‑3份、增稠剂0‑3份。

【技术特征摘要】
1.一种花纹陶瓷砖，由坯料和釉料加工而成，其特征在于，所述釉料由如下重量配比的基本组分配制而成：氧化钙5-10份、碳酸氢钠5-10份、云母粉10-30份、氧化锂10-30份、、氧化镁5-15份、氧化铝5-15份、颜料10-20份、膨润土20-50份、复合触变剂0-3份、分散剂0-3份、增稠剂0-3份。2.根据权利要求1所述的一种花纹陶瓷砖，其特征是，所述氧化铝为10份。3.根据权利要求2所述的一种花纹陶瓷砖，其特征是，所述颜料为15份。4.根据...

【专利技术属性】
技术研发人员：黄岳娇，
申请(专利权)人：黄岳娇，
类型：发明
国别省市：广东,44