本发明专利技术公开了一种锰锌铁氧体磁环及其制备方法，所述锰锌铁氧体磁环应用于逆变弧焊机、DC/DC转换器及电源用变压器，包括以摩尔百分含量计算的如下主成分：Fe2O3 53～54mol%；ZnO 7～9mol%；MnO 37～40mol%。通过上述方式，本发明专利技术能够满足电源变压器电感高和叠加高的要求，有利于变压器器件的储能和功率转化，提高其效率。

A manganese zinc ferrite magnetic ring and its preparation method

The invention discloses a manganese zinc ferrite magnetic ring and its preparation method. The manganese zinc ferrite magnetic ring is applied to the inverter welding machine, DC/DC converter and power transformer, including the following main components calculated by the content of mole percent: Fe2O3 53 to 54mol%; ZnO 7 to 9mol%; MnO 37 to 40mol%. Through the above methods, the invention can meet the requirements of the high inductance and high superposition of the power transformer, and is beneficial to the energy storage and power conversion of the transformer device, and the efficiency of the transformer can be improved.

【技术实现步骤摘要】
一种锰锌铁氧体磁环及其制备方法
本专利技术涉及磁环领域，特别是涉及一种锰锌铁氧体磁环及其制备方法。
技术介绍
随着电子信息产业迅速的发展，作为其所用的锰锌铁氧体磁芯电子元件，要求承载的功率大、发热少、噪音小、作为逆变弧焊机中主变压器的芯体磁环提出了更高的要求，常温条件下电感高，直流叠加高。现有的锰锌铁氧体磁环的检测数据如下表：原逆变弧焊机电源变压器中使用的EC型锰锌铁氧体将被淘汰，取代该EC型锰锌铁氧体的锰锌铁氧体磁环，从磁路方面讲是有贡献的，但从绕线方面，对芯体的温升、散热是不利的。我们对这些指标进行研究和分析得出，叠加电感主要提高芯体磁环的饱和磁通密度，电感对应的磁环芯体的导磁率。综上所述，为解决这些问题和客户的要求，应制作一种锰锌铁氧体的磁环和材料，以达到变压器使用下，常温下电感高和叠加高的要求；同时，克服使用磁环芯体带来的不利因数。
技术实现思路
本专利技术主要解决的技术问题是：针对现有技术的不足，提供一种锰锌铁氧体磁环，能够满足电源变压器常温下电感高和叠加高的要求，有利于变压器器件的储能和功率转化，提高其效率。为解决上述技术问题，本专利技术采用的一个技术方案是：提供一种锰锌铁氧本文档来自技高网...

【技术保护点】
一种锰锌铁氧体磁环，应用于逆变弧焊机、DC/DC转换器及电源用变压器，其特征在于，包括以摩尔百分含量计算的如下主成分：Fe2O3   53～54mol%；ZnO    7～9mol%；MnO    37～40mol%。

【技术特征摘要】
1.一种锰锌铁氧体磁环，应用于逆变弧焊机、DC/DC转换器及电源用变压器，其特征在于，包括以摩尔百分含量计算的如下主成分：Fe2O353～54mol%；ZnO7～9mol%；MnO37～40mol%。2.根据权利要求1所述的锰锌铁氧体磁环，其特征在于，进一步包括以摩尔百分含量计算的如下添加剂中的一种或多种：Co2O30.3～0.5mol%；Nb2O50.02～0.04mol%；CaCO30.04～0.08mol%；ZrO20.01～0.03mol%；SiO20.005～0.1mol%；TiO20.05～0.10mol%；NiO0.02～0.1mol%。3.根据权利要求1所述的锰锌铁氧体磁环，其特征在于，在H=10KHZ，0.1V，0.5A，25℃条件下，所述锰锌铁氧体磁环的叠加电感大于35%。4.根据权利要求1所述的锰锌铁氧体磁环，其特征在于...