The invention relates to the technical field of decorative materials, and discloses a flexible decorative wall material for removing formaldehyde, including the following components of mass percentage: acrylic emulsion or dispersible latex powder: 3 to 30%: inorganic fillers: 20 to 60%; quartz sand: 30 ~ 60%; urea: 2 to 5%; chitosan: 2 to 10%; nanometer TiO2:2 ~ 10%; lysine: 2 ~ 5%; pigment: 0 ~ 3%; thickener: 0 ~ 1%; hydrophobicity: 0 ~ 1%. Urea, chitosan and lysine all have active hydroxyl groups, which react with formaldehyde and decompose formaldehyde. The other purpose of the invention is to disclose a preparation method of the flexible decorative wall material for removing formaldehyde. By adding a formaldehyde catcher and a light touch enzyme to the flexible decorative wall material, the invention can thoroughly remove the formaldehyde adsorbed by the flexible decorative wall material, and will not cause two pollution.
【技术实现步骤摘要】
一种可清除甲醛的柔性装饰墙材及其制备方法
本专利技术涉及装饰材料
，具体地说是一种可清除甲醛的柔性装饰墙材及其制备方法。
技术介绍
柔性装饰片材本身为多孔结构，有一定吸附甲醛的作用，但其所吸附的甲醛饱和后在一定条件下会释放出来，造成二次污染。因此，亟需开发一种能够彻底清除甲醛、不会造成二次污染的柔性装饰墙材。
技术实现思路
针对上述技术问题，本专利技术公开一种可清除甲醛的柔性装饰墙材及其制备方法。本专利技术为实现上述目的，采取以下技术方案予以实现：一种可清除甲醛的柔性装饰墙材，包括质量百分比的以下组分：丙烯酸乳液或可分散性乳胶粉：3～30％：无机填料：20～60％；石英砂：30～60％；尿素：2～5％；壳聚糖：2～10％；纳米TiO2：2～10％；赖氨酸：2～5％；颜料：0～3％；增稠剂：0～1％；憎水剂：0～1％。优选地，根据权利要求1所述的一种可清除甲醛的柔性装饰墙材，其特征在于，所述无机填料为水泥、矿粉、石粉、泥粉、粉煤灰、硅灰粉、高岭土中的一种或一种以上的组合。本专利技术的另一目的在于公开一种上述清除甲醛的柔性装饰墙材的制备方法，具体步骤如下：将配方中的...
【技术保护点】
一种可清除甲醛的柔性装饰墙材，其特征在于，包括质量百分比的以下组分：丙烯酸乳液或可分散性乳胶粉：3～30％；无机填料：20～60％；石英砂：30～60％；尿素：2～5％；壳聚糖：2～10％；纳米TiO2：2～10％；赖氨酸：2～5％；颜料：0～3％；增稠剂：0～1％；憎水剂：0～1％。
【技术特征摘要】
1.一种可清除甲醛的柔性装饰墙材，其特征在于，包括质量百分比的以下组分：丙烯酸乳液或可分散性乳胶粉：3～30％；无机填料：20～60％；石英砂：30～60％；尿素：2～5％；壳聚糖：2～10％；纳米TiO2：2～10％；赖氨酸：2～5％；颜料：0～3％；增稠剂：0～1％；憎水剂：0～1％。2.根据权利要求1所述的一种可清除甲醛的柔性装饰墙材，其特征在于，所...
【专利技术属性】
技术研发人员：石磊，
申请(专利权)人：广西福美新材料有限公司，
类型：发明
国别省市：广西,45