一种新型骨诱导再生医用膜及其制备方法技术
A new type of bone induction and regeneration medical membrane and its preparation method
The invention discloses a novel bone induced regenerative medical membrane and its preparation method, which belongs to the biological material technology field of tissue engineering. It is made up of alginate, chitosan and bone induced components and is prepared by a hybrid electrospinning technology. The content of the bone inducible component is 1.0wt% ~10.0wt%, the alginate and the quality of chitosan. The ratio is 3:1~1:1, and the basic principle of bone defect treatment is invented. The electrospun technique is used to prepare the bone induced regenerative medical membrane, which has the dual functions of anti-inflammatory and promoting bone tissue regeneration.
【技术实现步骤摘要】
一种新型骨诱导再生医用膜及其制备方法
：本专利技术属于组织工程的生物材料
，具体涉及一种新型骨诱导再生医用膜及其制备方法。
技术介绍
：骨缺损修复主要治疗办法是通过植入骨替代物以期获得原骨部分功能，但最终还是需要骨组织再生填补缺损部位。一般方法通过在骨替代物中添加促进骨组织再生的骨诱导成分，但骨缺损通常伴有炎症反应，在未控制的炎症状态下，骨组织的再生和重建不可能实现，因此，有效控制骨缺损部位炎症反应是骨组织再生的前提条件。
技术实现思路
本专利技术针对现有技术中存在的上述缺点，提出一种制备新型骨诱导再生医用膜的制备方法，本专利技术利用骨缺损治疗基本原理，利用静电纺丝技术制备骨诱导再生医用膜，具有抗菌消炎和促进骨组织再生的双重功能。为实现上述目的，本专利技术的技术方案为：一种制备新型骨诱导再生医用膜由藻酸盐、壳聚糖和骨诱导成分组成，经过混合静电纺丝技术制备而成，所述骨诱导成分含量为1.0wt%~10.0wt%，所述藻酸盐与壳聚糖的质量比为3:1~1:1。优选的，所述骨诱导成分为碱性成纤维细胞生长因子bFGF和骨形态发生蛋白按照质量比为2:1~1:2混合而成。优选的...
【技术保护点】
一种新型骨诱导再生医用膜，其特征在于，由藻酸盐、壳聚糖和骨诱导成分组成，经过混合静电纺丝技术制备而成，所述骨诱导成分含量为1.0wt%~10.0wt%，所述藻酸盐与壳聚糖的质量比为3:1~1:1。
【技术特征摘要】
1.一种新型骨诱导再生医用膜，其特征在于，由藻酸盐、壳聚糖和骨诱导成分组成，经过混合静电纺丝技术制备而成，所述骨诱导成分含量为1.0wt%~10.0wt%，所述藻酸盐与壳聚糖的质量比为3:1~1:1。2.根据权利要求1所述的新型骨诱导再生医用膜，其特征在于，所述骨诱导成分为碱性成纤维细胞生长因子bFGF和骨形态发生蛋白按照质量比为2:1~1:2混合而成。3.根据权利要求2所述的新型骨诱导再生医用膜，其特征在于，所述骨诱导成分为碱性成纤维细胞生长因子bFGF和骨形态发生蛋白按照质量比为2:1混合而成。4.根据权利要求1所述的新型骨诱导再生医用膜，其特征在于，所述藻酸盐与壳聚糖的质量比为3:1。5.根据权利要求1所述的新型骨诱导再生医用膜，其特征在于，医用膜的厚度为2μm~5μm。6.根据权利要求1所述的新型骨诱导再生医用膜，其特征在于，藻酸盐纤维和壳聚糖纤维的直径为1μm~4μm。7.如权...
【专利技术属性】
技术研发人员：陈锦涛，韦加娜，吴帅，
申请(专利权)人：广东泰宝医疗器械技术研究院有限公司，
类型：发明
国别省市：广东,44