一种Rh@CuSiO3芯鞘结构催化剂制备方法技术
A method for preparation of Rh@CuSiO3 core sheath catalyst
The invention discloses a Rh@CuSiO3 nano structure hydrogenation catalyst and a preparation method thereof. The preparation process of the Rh@CuSiO3 hydrogenation catalyst is: first, the synthesis of silicate nanotubes in the ethanol water system by hydrothermal method is used to control the synthesis of copper nanotubes by controlling the experimental conditions. Then, the metal rhodium is loaded in the copper nanotube by impregnation. The Rh@CuSiO3 hydrogenation catalyst prepared by this method can improve the dispersion of the active component and its interaction with the carrier through the structure limiting effect of the coupling core sheath material and the synergistic effect between its components, thus enhancing the catalytic hydrogenation performance, which has a wide application prospect.
【技术实现步骤摘要】
一种Rh@CuSiO3芯鞘结构催化剂制备方法
本专利技术涉及一种Rh@CuSiO3纳米结构贵金属催化剂及其制备方法，该催化剂利用限域作用使Rh物种以纳米颗粒形式存在，具有较高的Rh活性组分数量和热稳定性，可用于CO2催化加氢反应。
技术介绍
CO2催化加氢反应能够转化生产多种低碳化合物，对环境保护和工业生产皆有重要意义。目前为止，CO2催化加氢的催化剂通常为多相体系，主要可以分为铜、贵金属以及双金属为活性组分的负载型催化剂。其中，Rh等典型的贵金属具有较强的H2解离和加氢反应能力，而金属Rh在元素周期表中处于易使CO分解形成高级碳氢化合物的元素（Fe、Co）和不使CO分解产生甲醇的元素（Pd，Pt和Ir）之间，具有独特的生成C2含氧化合物的特性，有利于使CO氢化形成甲醇、乙醇等醇类含氧化合物。因此，Rh基催化剂是目前研究最广泛的CO2催化加氢制低碳醇的非均相贵金属催化剂。然而，Rh基催化剂在CO2加氢过程中容易引起晶粒迁移、烧结和Rh活性组分不稳定，从而导致反应活性低、稳定性差、反应条件苛刻等问题。因此，设计构筑特殊形貌结构和表面化学性质的新型Rh基催化剂，通过结...
【技术保护点】
一种Rh@CuSiO3催化剂，其特征在于：新型芯鞘结构加氢催化剂。
【技术特征摘要】
1.一种Rh@CuSiO3催化剂，其特征在于：新型芯鞘结构加氢催化剂。2.根据权利要求1所述的Rh@CuSiO3加氢催化剂的制备方法，其特征在于包括以下步骤：1）制备硅酸铜鞘腔：将1.5克Cu(NO3)2•6H2O加入水中溶解，然后加入25%的氨水使溶液先生成沉淀然后再溶解，随后加入乙醇搅拌，10min后，将之前配好的0.5mol/L的NaSiO3•9H2O溶液加入10mL到溶液中，形成蓝色沉淀，搅拌180min，之后转移至150mL水热釜中，移至烘箱中473K下水热处理12~36小时，然后取出冷却、过滤、洗涤、干燥、焙烧后，既得CuPNTs；2）金属铑的填充：将0.1g固体RhCl3加入25ml无水乙醇中，超声，待RhCl3固体全部溶解后，倒入事先称...
【专利技术属性】
技术研发人员：岳海荣，廖瑞，唐思扬，刘长军，梁斌，
申请(专利权)人：四川大学，
类型：发明
国别省市：四川,51