The invention discloses a high cold resistant PVC product and a preparation method thereof. The invention can effectively improve the cold resistance of PVC plastic and meet the low temperature requirement by adjusting PVC resins and auxiliaries. In the invention, the material and the amount of material for PVC material and material are made scientifically. Each component is an organic whole, and the synergistic effect will be produced between the raw materials. The plasticization of the PVC is very good, the flexibility of the PVC product is increased and the cold resistance performance is more prominent.
【技术实现步骤摘要】
一种高耐寒PVC制品及其制备方法
本专利技术属于PVC应用
，具体涉及一种高耐寒PVC制品及其制备方法。
技术介绍
PVC具有良好的物理及机械性能，但其耐寒和低温抗冲击性能较差，限制了PVC材料在某些领域的使用。
技术实现思路
专利技术目的：为了解决现有技术的不足，本专利技术提供了一种高耐寒PVC制品及其制备方法。技术方案：一种高耐寒PVC制品，所述的高耐寒PVC制品由PVC底料和PVC面料所制成；所述PVC底料由以下原料制成：重量份数为100份的聚氯乙烯树脂、重量份数为10份的碳酸钙、重量份数为85-95份的邻苯二甲酸酯、重量份数为4-6份的粉体稳定剂和重量份数为5份的小料；PVC面料由以下原料制成：重量份数为100份的聚氯乙烯树脂、重量份数为10份的碳酸钙、重量份数为85-95份的邻苯二甲酸酯、重量份数为2-3份的液体稳定剂和重量份数为8-10份的小料。作为优化：所述粉体稳定剂为钙钡锌综合粉体稳定剂。作为优化：所述小料为色料及高弹性改质剂，具体组份为：环保材TPU/TPR，配比：10-15份。作为优化：所述液体稳定剂为钡锌液体稳定剂。一种根据所述的高耐寒PV...
【技术保护点】
一种高耐寒PVC制品，其特征在于：所述的高耐寒PVC制品由PVC底料和PVC面料所制成；所述PVC底料由以下原料制成：重量份数为100份的聚氯乙烯树脂、重量份数为10份的碳酸钙、重量份数为85‑95份的邻苯二甲酸酯、重量份数为4‑6份的粉体稳定剂和重量份数为5份的小料；PVC面料由以下原料制成：重量份数为100份的聚氯乙烯树脂、重量份数为10份的碳酸钙、重量份数为85‑95份的邻苯二甲酸酯、重量份数为2‑3份的液体稳定剂和重量份数为8‑10份的小料。
【技术特征摘要】
1.一种高耐寒PVC制品，其特征在于：所述的高耐寒PVC制品由PVC底料和PVC面料所制成；所述PVC底料由以下原料制成：重量份数为100份的聚氯乙烯树脂、重量份数为10份的碳酸钙、重量份数为85-95份的邻苯二甲酸酯、重量份数为4-6份的粉体稳定剂和重量份数为5份的小料；PVC面料由以下原料制成：重量份数为100份的聚氯乙烯树脂、重量份数为10份的碳酸钙、重量份数为85-95份的邻苯二甲酸酯、重量份数为2-3份的液体稳定剂和重量份数为8-10份的小料。2.根据权利要求1所述的高耐寒PVC制品，其特征在于：所述粉体稳定剂为钙钡锌综合粉体稳定剂。3.根据权利要求1所述的高耐寒PVC制品，其特征在于：所述小料为色料及高弹性改质剂,具体组份为：环保材TPU/TPR，配比：10-15份。4.根据权利要求1所述的高耐寒PVC制品，其特征在于：所述液体稳定剂为钡锌液体稳定剂。5.一种根据权利要求1所述的高耐寒PVC制品的制备方法，其特征在于：包括PVC底料生产步骤、PVC面料生产步骤和贴合步骤，发泡，后处理；具体操作如下：A.所述PVC底料生产步骤依次包括如下工序：(1)将聚氯乙烯树脂、碳酸钙、邻苯二甲酸酯、粉体稳定剂混合，得到主料；...
【专利技术属性】
技术研发人员：吕卓颖，徐赢赢，
申请(专利权)人：南亚塑胶工业南通有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。