一种螺母的制造工艺制造技术
Manufacturing process of a nut
The invention discloses a manufacturing process of a nut, including the following steps, melting copper and iron, melting copper in a melting furnace, then putting iron in another furnace, heating the furnace to about 1200 degrees, if the temperature is too high, and if it is too low, it is not good for the combination of copper and water, and the copper is melted after melting. The copper water is heated and heated to about 1600 degrees. If the temperature is too high, the copper will also have oxidation layer. It is too low to combine with the iron. The nut die is paving and the molten iron is poured into the mold first. Then the copper water is poured into the mold, and the steel is placed in the mold after cooling. The invention has the shape of the ladder for the large tensile strength. The anti slip groove is designed to increase the strength and the shape of the nut is not easy to burst.
【技术实现步骤摘要】
一种螺母的制造工艺
本专利技术涉及螺母的制造工艺
，尤其涉及一种螺母的制造工艺。
技术介绍
螺母的种类很多，有典型的六角螺母、外加螺母、槽形螺母、支点螺母、锁紧螺母、活动接头螺母、外套螺母、小圆螺母、连接螺母、六角薄螺母、支板螺母、双耳自锁螺母等；在航空发动机上起着连接零件的作用，主要负责管路部件、密封零件的连接及各部件的连接，其加工质量的好坏对其部件的传动性、紧固性、密封性有着直接的影响，直接影响到发动机的整体性能，因此保证其加工质量是零件加工中的技术关键。市场经济的前提下，一切都是为能创造出更多的财富和提高劳动率为目的，同样的加工方法的选择一般考虑的是在保证工件加工要求的前提下，提高工件的加工效率和经济性，而在具体的选择上，一般根据机械加工资料和工人的经验来确定。由于方法的多种多样，工人在选择时一般结合具体的工件和现场的加工条件来确定最佳的加工方案。现有的螺母内的铜芯呈圆柱形的，且此类螺母在应用的过程中容易出现爆裂的现象，本专利技术的铜呈梯子形状是为了抗拉强度大幅度提高，防滑槽是为了加大了抗强度，且螺母形状呈椎体不容易爆破。
技术实现思路
专利技术目的：本专...
【技术保护点】
一种螺母的制造工艺，其特征在于，包括如下步骤:第一步：熔化铜和铁，首先把铜放入熔炉中熔化，接着将铁放入另外熔炉中，将熔炉加热至1200度左右，将铜熔化后的铜水进行加热，加热至1600度左右；第二步：铸模，将螺母模具铺平，先将铁水倒入模具中，接着将铜水倒入模具中，待冷却后，将钢放置进去。
【技术特征摘要】
1.一种螺母的制造工艺，其特征在于，包括如下步骤:第一步：熔化铜和铁，首先把铜放入熔炉中熔化，接着将铁放入另外熔炉中，将熔炉加热至1200度左右，将铜熔化后的铜水进行加热，加热至1600度左右；第二步：铸模，将螺母模具铺平，先将铁水倒入模具中，接着将铜水倒入模具中，待冷却后，将钢放置进去。2.根据权利要求1所述一种螺母的制造工艺，其特征在于，所述模具内设有凹槽，所述凹槽呈椎...
【专利技术属性】
技术研发人员：朱建龙，
申请(专利权)人：盐城楷翔钻采配件有限公司，
类型：发明
国别省市：江苏,32
-